Oxidation and hot corrosion behavior of NiCrAlYSi plus NiAl/cBN abrasive coating
文献类型：期刊论文
| 作者 | Liu, Y. D.1,2; Sun, J.3; Pei, Z. L.1; Li, W.1,2; Liu, J. H.1,2; Gong, J.1; Sun, C.1 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2020-05-01 |
| 卷号 | 167页码:13 |
| ISSN号 | 0010-938X |
| 关键词 | Abrasive coating cBN particles Electroplating Oxidation Hot corrosion |
| DOI | 10.1016/j.corsci.2020.108486 |
| 通讯作者 | Pei, Z. L.(pei@imr.ac.cn) ; Sun, C.(csun@imr.ac.cn) |
| 英文摘要 | In order to improve the oxidation and hot corrosion resistance of blades tip as well as the sealing performance of gas turbine engine, a NiCrAlYSi + NiAl/cBN abrasive coating was prepared by combining arc ion plating, electroplating and above-pack aluminisation. Oxidation and hot corrosion behavior of the abrasive coating were investigated. Results indicated that the abrasive coating showed lower oxidation and degradation rate at 900 degrees C. NaCl aggravated the corrosion extent via cyclic chlorination/oxidation reaction, and the cBN/metallic coating interface also played a crucial role as a shortcut of the corrosive media. Besides, the oxidation and hot corrosion mechanisms were discussed. |
| 资助项目 | Tianjin Major Science and Technology Project of Military-Civil Integration[18ZXJMTG00050] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| WOS记录号 | WOS:000525869800008 |
| 资助机构 | Tianjin Major Science and Technology Project of Military-Civil Integration |
| 源URL | [http://ir.imr.ac.cn/handle/321006/138258]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Pei, Z. L.; Sun, C. |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, 72 Wenhua Rd, Shenyang 110016, Peoples R China 3.Qilu Univ Technol, Shandong Acad Sci, Adv Res Inst Multidisciplinary Sci, 3501 Daxue Rd, Jinan 250353, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Y. D.,Sun, J.,Pei, Z. L.,et al. Oxidation and hot corrosion behavior of NiCrAlYSi plus NiAl/cBN abrasive coating[J]. CORROSION SCIENCE,2020,167:13. |
| APA | Liu, Y. D..,Sun, J..,Pei, Z. L..,Li, W..,Liu, J. H..,...&Sun, C..(2020).Oxidation and hot corrosion behavior of NiCrAlYSi plus NiAl/cBN abrasive coating.CORROSION SCIENCE,167,13. |
| MLA | Liu, Y. D.,et al."Oxidation and hot corrosion behavior of NiCrAlYSi plus NiAl/cBN abrasive coating".CORROSION SCIENCE 167(2020):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。