Microstructure and composition evolution of a single-crystal superalloy caused by elements interdiffusion with an overlay NiCrAlY coating on oxidation
文献类型：期刊论文
| 作者 | Yang, Lanlan2; Chen, Minghui1; Wang, Jinlong1; Qiao, Yanxin2; Guo, Pingyi2; Zhu, Shenglong3; Wang, Fuhui1 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2020-05-15 |
| 卷号 | 45页码:49-58 |
| 关键词 | Single-crystal superalloys NiCrAlY coating High-temperature oxidation Arc ion plating Elements interdiffusion Microstructure |
| ISSN号 | 1005-0302 |
| DOI | 10.1016/j.jmst.2019.11.017 |
| 通讯作者 | Chen, Minghui(mhchen@mail.neu.edu.cn) |
| 英文摘要 | MCrAlY (M=Ni and/or Co) overlay coating is widely used as a protective coating against high temperature oxidation and corrosion. However, due to its big difference in chemical composition with the underlying superalloy, elements interdiffusion occurs inevitably. One of the direct results is the formation of interdiffusion zone (IDZ) and secondary reaction zone (SRZ) with a high density of fine topological closed-packed phases (TCPs), weakening dramatically the mechanical properties of the alloy substrate. It is by now the main problem of modern high-temperature metallic coatings, but there are still hardly any reports studying the formation, growth and transformation of IDZ and SRZ in deep, as well as the precipitation of TCPs. In this work, a typical NiCrAlY coating is deposited by arc ion plating on a single-crystal superalloy N5. Elements interdiffusion between them and its relationship on microstructure were clarified. Cr rather than Al from the coating diffuses into the alloy at high temperatures and segregates immediately beneath their interface, contributing largely to the formation of IDZ. Simultaneously, diffusion of Ni from the deep alloy to IDZ leads to the formation and continuous expansion of SRZ. (C) 2020 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 资助项目 | National Natural Science Foundation of China[51671053] ; National Natural Science Foundation of China[51801021] ; Ministry of Industry and Information Technology Project[MJ-2017-J-99] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000526956200006 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| 资助机构 | National Natural Science Foundation of China ; Ministry of Industry and Information Technology Project |
| 源URL | [http://ir.imr.ac.cn/handle/321006/138543]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen, Minghui |
| 作者单位 | 1.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 2.Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Jiangsu, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang, Lanlan,Chen, Minghui,Wang, Jinlong,et al. Microstructure and composition evolution of a single-crystal superalloy caused by elements interdiffusion with an overlay NiCrAlY coating on oxidation[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2020,45:49-58. |
| APA | Yang, Lanlan.,Chen, Minghui.,Wang, Jinlong.,Qiao, Yanxin.,Guo, Pingyi.,...&Wang, Fuhui.(2020).Microstructure and composition evolution of a single-crystal superalloy caused by elements interdiffusion with an overlay NiCrAlY coating on oxidation.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,45,49-58. |
| MLA | Yang, Lanlan,et al."Microstructure and composition evolution of a single-crystal superalloy caused by elements interdiffusion with an overlay NiCrAlY coating on oxidation".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 45(2020):49-58. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。