Interfacial modification and cyclic ablation behaviors of a SiC/ZrB2-SiC/SiC triple-layer coating for C/SiC composites at above 2000 degrees C

文献类型：期刊论文

作者Tane, Pengju1,2,3; Hu, Chenglong3; Pang, Shengyang3; Li, Jian3; Wang, Lei1,2; Tang, Sufang3
刊名CORROSION SCIENCE
出版日期2020-06-01
卷号169页码:9
关键词Ceramic matrix composite Thermal cycling Oxidation
ISSN号0010-938X
DOI10.1016/j.corsci.2020.108604
通讯作者Wang, Lei(wanglei@mail.neu.cn) ; Tang, Sufang(sftang@imr.ac.cn)
英文摘要A SiC/ZrB2-SiC/SiC triple-layer coating was fabricated successively by chemical vapor deposition (CVD), slurry brushing-sintering and CVD for C/SiC composites. To enhance the cyclic ablation resistance, a pre-oxidation treatment on the inner SiC layer was performed. The bonding strength of the coating with pre-oxidation at 1600 degrees C is significantly improved to 32 MPa, 77.8 % greater than that of the untreated specimen. The coating can endure 5 ablation cycles from 2050 degrees C to room temperature without peeling off and displays a small spalling area of 18 mm(2) after 6 cycles. The cyclic ablation mechanisms are discussed in detail.
资助项目Major Program of Aerospace Advanced Manufacturing Technology Research Foundation of NSFC ; CASC, China[U1537204] ; National Natural Science Foundations of China[51802313] ; National Natural Science Foundations of China[51902315] ; National Science and Technology Major Project[2017-VI-0020-0093] ; National Key R&D Program of China[2018YFF01013600] ; LiaoNing Revitalization Talents Program ; Research Fund of Youth Innovation Promotion Association of CAS, China[2014171]
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
语种英语
WOS记录号WOS:000530031900009
出版者PERGAMON-ELSEVIER SCIENCE LTD
资助机构Major Program of Aerospace Advanced Manufacturing Technology Research Foundation of NSFC ; CASC, China ; National Natural Science Foundations of China ; National Science and Technology Major Project ; National Key R&D Program of China ; LiaoNing Revitalization Talents Program ; Research Fund of Youth Innovation Promotion Association of CAS, China
源URL[http://ir.imr.ac.cn/handle/321006/138676]  
专题金属研究所_中国科学院金属研究所
通讯作者Wang, Lei; Tang, Sufang
作者单位1.Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China
2.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China
3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714		 Tane, Pengju,Hu, Chenglong,Pang, Shengyang,et al. Interfacial modification and cyclic ablation behaviors of a SiC/ZrB2-SiC/SiC triple-layer coating for C/SiC composites at above 2000 degrees C[J]. CORROSION SCIENCE,2020,169:9.
APA Tane, Pengju,Hu, Chenglong,Pang, Shengyang,Li, Jian,Wang, Lei,&Tang, Sufang.(2020).Interfacial modification and cyclic ablation behaviors of a SiC/ZrB2-SiC/SiC triple-layer coating for C/SiC composites at above 2000 degrees C.CORROSION SCIENCE,169,9.
MLA Tane, Pengju,et al."Interfacial modification and cyclic ablation behaviors of a SiC/ZrB2-SiC/SiC triple-layer coating for C/SiC composites at above 2000 degrees C".CORROSION SCIENCE 169(2020):9.

入库方式： OAI收割

来源：金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。