Formation Mechanism of Microstructural Non-uniformity in the Hot Working of Commercial-Scale Electro-slag Remelted Alloy 690 Ingots
文献类型：期刊论文
| 作者 | Wang, Min1; Yi, Haoyu2; Zhao, Xia1; Zhang, Long1; Ma, Yingche1; Liu, Kui1 |
| 刊名 | METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
 |
| 出版日期 | 2020-05-23 |
| 卷号 | 51期号:8页码:12 |
| ISSN号 | 1073-5623 |
| DOI | 10.1007/s11661-020-05813-1 |
| 通讯作者 | Ma, Yingche(ycma@imr.ac.cn) |
| 英文摘要 | Microstructural non-uniformity in the wrought material of Alloy 690 is investigated in this study by analyzing the dissolution behavior of intergranular carbides, performing laboratorial forgings to explore the microstructural evolution rules and conduct industrial forgings to verify the laboratorial results. The intergranular carbides in Alloy 690 ESR ingots cannot be fully dissolved at a temperature < 1473 K (1200 degrees C), and undissolved carbides cause the appearance of carbide strips in the forged microstructure. Carbide strips are confirmed to be responsible for the formation of fine-grain bands in the wrought material by restricting the growth of nearby grains during annealing treatment. Industrial forgings agree well with the laboratorial tests, and it is recommended that in industrial practice the soaking temperature of large ESR ingots should be set between 1473 K and 1493 K (1200 degrees C and 1220 degrees C) for better carbide dissolution, and an evident ingot temperature drop prior to deformation should be avoided. |
| 资助项目 | National Natural Science Foundation of China[51801211] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000534991400004 |
| 出版者 | SPRINGER |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/138932]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ma, Yingche |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 2.China Nucl Power Technol Res Inst, Shenzhen 518000, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Min,Yi, Haoyu,Zhao, Xia,et al. Formation Mechanism of Microstructural Non-uniformity in the Hot Working of Commercial-Scale Electro-slag Remelted Alloy 690 Ingots[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,2020,51(8):12. |
| APA | Wang, Min,Yi, Haoyu,Zhao, Xia,Zhang, Long,Ma, Yingche,&Liu, Kui.(2020).Formation Mechanism of Microstructural Non-uniformity in the Hot Working of Commercial-Scale Electro-slag Remelted Alloy 690 Ingots.METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,51(8),12. |
| MLA | Wang, Min,et al."Formation Mechanism of Microstructural Non-uniformity in the Hot Working of Commercial-Scale Electro-slag Remelted Alloy 690 Ingots".METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE 51.8(2020):12. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。