Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C
文献类型：期刊论文
| 作者 | Yu, Zhongdi1,2; Chen, Minghui1,2; Li, Fengjie1,2; Zhu, Shenglong3; Wang, Fuhui1,2 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2020-04-01 |
| 卷号 | 165页码:10 |
| 关键词 | Stainless steel Molten zinc alloy EPMA Liquid-metal corrosion Tribo-corrosion |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2019.108411 |
| 通讯作者 | Chen, Minghui(mhchen@mail.neu.edu.cn) |
| 英文摘要 | The failure of 316 stainless steel under tribo-corrosion in molten zinc alloy (Zn-0.2Al, wt%) at 460 degrees C was investigated and compared with corrosion or the sole wear. In the absence of wear, intact Fe2Al5Znx layer forms and protects the steel from dramatic corrosion. Without liquid-metal corrosion, the steel suffers from plastic deformation on friction and slight adhesive wear. While for tribo-corrosion, the synergy of corrosion and wear accounts for 90 % of material loss. Firstly, corrosion generates a brittle scale and leads to embrittlement at subsurface, which accelerate wear. Secondly, wear promotes the formation of less-protective FeZn10 scale, accelerating corrosion. |
| 资助项目 | National Key R&D Program of China[2017YFB0306100] ; National Natural Science Foundation of China[51871051] ; Fundamental Research Funds for the Central Universities[N180212008] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000518488800043 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | National Key R&D Program of China ; National Natural Science Foundation of China ; Fundamental Research Funds for the Central Universities |
| 源URL | [http://ir.imr.ac.cn/handle/321006/138971]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen, Minghui |
| 作者单位 | 1.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 2.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yu, Zhongdi,Chen, Minghui,Li, Fengjie,et al. Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C[J]. CORROSION SCIENCE,2020,165:10. |
| APA | Yu, Zhongdi,Chen, Minghui,Li, Fengjie,Zhu, Shenglong,&Wang, Fuhui.(2020).Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C.CORROSION SCIENCE,165,10. |
| MLA | Yu, Zhongdi,et al."Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C".CORROSION SCIENCE 165(2020):10. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。