Synthesis of monolithic carbon aerogels with high mechanical strength via ambient pressure drying without solvent exchange
文献类型：期刊论文
| 作者 | Yang, Zhi1,2; Li, Jian2; Xu, Xiaojing3; Pang, Shengyang2; Hu, Chenglong2; Guo, Penglei1,2; Tang, Sufang2; Cheng, Hui-Ming2 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2020-08-01 |
| 卷号 | 50页码:66-74 |
| ISSN号 | 1005-0302 |
| 关键词 | Carbon aerogels Ambient pressure drying High mechanical strength Thermal insulation |
| DOI | 10.1016/j.jmst.2020.02.013 |
| 通讯作者 | Tang, Sufang(sftang@imr.ac.cn) |
| 英文摘要 | A simple, fast and cost-effective method for monolithic carbon aerogels (CAs) preparation was proposed through sol-gel polycondensation of resorcinol with formaldehyde in a basic aqueous solution followed by ambient pressure drying without solvent exchange, and carbonization. The microstructure and network strength of CAs were tailored by adjusting the catalyst concentration ([resorcinol]/[sodium carbonate] in the range of 300-2000), water content ([deionized water]/[resorcinol] equals to 17 and 24, respectively), and gelation temperature (T(gel )in the range of 30-90 degrees C). Resultantly, the CAs with a wide range of density (0.30-1.13 g/cm(3)), high specific surface area (465-616 m(2)/g), high compressive strength (6.5-147.4 MPa) and low thermal conductivity (0.065-0.120 W m(-1) K-1) were obtained in this work. Moreover, the largesized CAs (100 x 100 x 20 mm(3)) can also be prepared by this method since the formed robust skeleton network can resist shrinkage/collapse of pore structure and prevent cracking during drying. The improved mechanical strength and monolithic forming abilities could be mainly attributed to the uniform arrangement of carbon particles and pores, fine particle size, abundant network structure and enhanced particle neck. (C) 2020 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 资助项目 | Major Program ofAerospace Advanced Manufacturing Technology Research Foundation of NSFC ; CASC, China[U1537204] ; National Natural Science Foundation of China[51802313] ; National Natural Science Foundation of China[51902315] ; National Science and Technology Major Project[2017-VI-0020-0093] ; Research Fund of Youth Innovation Promotion Association of CAS, China[2014171] ; National Key R&D Program of China[2018YFF01013600] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| WOS记录号 | WOS:000537588800007 |
| 资助机构 | Major Program ofAerospace Advanced Manufacturing Technology Research Foundation of NSFC ; CASC, China ; National Natural Science Foundation of China ; National Science and Technology Major Project ; Research Fund of Youth Innovation Promotion Association of CAS, China ; National Key R&D Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/139130]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Tang, Sufang |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 3.China Acad Launch Vehicle Technol, Aerosp Business Dept, Beijing 100076, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang, Zhi,Li, Jian,Xu, Xiaojing,et al. Synthesis of monolithic carbon aerogels with high mechanical strength via ambient pressure drying without solvent exchange[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2020,50:66-74. |
| APA | Yang, Zhi.,Li, Jian.,Xu, Xiaojing.,Pang, Shengyang.,Hu, Chenglong.,...&Cheng, Hui-Ming.(2020).Synthesis of monolithic carbon aerogels with high mechanical strength via ambient pressure drying without solvent exchange.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,50,66-74. |
| MLA | Yang, Zhi,et al."Synthesis of monolithic carbon aerogels with high mechanical strength via ambient pressure drying without solvent exchange".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 50(2020):66-74. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。