Corrosion Inhibition Behavior of 1-Hydroxyethylidene-1,1-Diphosphonic Acid on 20SiMn Steel in Simulated Concrete Pore Solution Containing CU
文献类型：期刊论文
| 作者 | Cao Fengting1,2; Wei Jie1; Dong Junhua1; Ke Wei1; Wang Tiegang2; Fan Qixiang2 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2020-06-01 |
| 卷号 | 56期号:6页码:898-908 |
| 关键词 | HEDP corrosion corrosion inhibitor adsorption simulated concrete pore solution |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2019.00382 |
| 通讯作者 | Dong Junhua(jhdong@imr.ac.cn) |
| 英文摘要 | The corrosion of steel rebar in concrete will be induced once the passive film is destroyed by chlorides or carbonation. Several techniques have been employed to reduce the corrosion so far. Among them, adding inhibitors is effective one because of its advantages, such as high efficiency and easy handling. 1-hydroxyethylidene-1,1-diphosphonic acid (HEDP), a typical organic phosphonic acid, is a low toxic corrosion inhibitor for steel and iron in neutral aerobic environment. This compound was first used as scale inhibitor in water treatment industry, such as cooling water circulation system. The molecule of HEDP has two phosphate groups, making it a powerful chelating ability with metallic ions. However, most of the current studies of HEDP focus on neutral or near-neutral systems, and there are few reports on the corrosion inhibition of steel reinforcement in alkaline environment. Therefore, it is not clear whether HEDP can play the role of corrosion inhibitor by protecting the passive film and resist foreign corrosive Cl-. In this work, the inhibition effect of HEDP towards 20SiMn steel was investigated in simulated concrete pore solution contaminated by Cl-(Sat.Ca(OH)(2)+1 mol/L NaCl) by electrochemical methods (corrosion potential, potentiodynamic polarization curves, EIS and Mott-Schottcky curves) and surface analysis techniques (SEM, XPS). The results showed that HEDP was a mixed inhibitor and its inhibition efficiency increased first and then decreased with the increase of concentration, the optimal concentration is 1.441x10(-4) mol/L. At the optimal concentration, HEDP could obviously enlarge the passive region, prolong the passive period of 20SiMn steel from 6 h to 9 h, and improve the charge-transfer resistance significantly with the inhibition efficiency around 46.45%-59.78%. When pitting corrosion occurs, HEDP could hinder its development with the inhibition efficiency over 93%. The inhibition mechanism was the preferential adsorption of HEDP over Cl- by forming a complete adsorption film outside the passive film of the steel. |
| 资助项目 | National Natural Science Foundation of China[51501201] ; National Natural Science Foundation of China[51801219] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000546975500010 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/139672]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Dong Junhua |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Tianjin Univ Technol & Educ, Sch Mech Engn, Tianjin Key Lab High Speed Cutting & Precis Machi, Tianjin 300222, Peoples R China |
| 推荐引用方式 GB/T 7714 | Cao Fengting,Wei Jie,Dong Junhua,et al. Corrosion Inhibition Behavior of 1-Hydroxyethylidene-1,1-Diphosphonic Acid on 20SiMn Steel in Simulated Concrete Pore Solution Containing CU[J]. ACTA METALLURGICA SINICA,2020,56(6):898-908. |
| APA | Cao Fengting,Wei Jie,Dong Junhua,Ke Wei,Wang Tiegang,&Fan Qixiang.(2020).Corrosion Inhibition Behavior of 1-Hydroxyethylidene-1,1-Diphosphonic Acid on 20SiMn Steel in Simulated Concrete Pore Solution Containing CU.ACTA METALLURGICA SINICA,56(6),898-908. |
| MLA | Cao Fengting,et al."Corrosion Inhibition Behavior of 1-Hydroxyethylidene-1,1-Diphosphonic Acid on 20SiMn Steel in Simulated Concrete Pore Solution Containing CU".ACTA METALLURGICA SINICA 56.6(2020):898-908. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。