Effect of Zr on solidification segregation behavior of K417G alloy and its anomalous effect during rapid cooling process
文献类型：期刊论文
| 作者 | Qi, Feng1,4; Yu, Lianxu3; Zhao, Guangdi2; Xin, Xin4; Zhang, Bin1; Sun, Wenru4 |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2020-09-15 |
| 卷号 | 835页码:9 |
| 关键词 | Zirconium Solidification (gamma plus gamma ') eutectic K417G |
| ISSN号 | 0925-8388 |
| DOI | 10.1016/j.jallcom.2020.155243 |
| 通讯作者 | Sun, Wenru(wrsun@imr.ac.cn) |
| 英文摘要 | Although Zr is classified as a beneficial element in superalloys, it noticeably increases the solidification segregation, worsens the as cast microstructure and lowers the melting point of the superalloys, but the detailed information about the behavior of Zr during the solidification remains unknown till now. In this paper, some evidences supporting the assumption that a film of Zr formed at the solid/liquid interface during solidification have been found, including the precipitation of ZrC, Zr-2 (SC) and Ni-Zr phases at the grain boundary or eutectic (gamma+ gamma') front, and the concentration of Zr at the crack surface formed at the final stage of the K417G alloy solidification. The Zr-rich film at the solid/liquid interface markedly lowers the solidification rate of K417G alloy, and decreases the content of Al, Ti, Cr and Mo in the dendrite core. As a result, the precipitation of (gamma+ gamma') eutectic is largely increased. Under water quenching conditions, the solidification of the final liquids contains two sequential eutectic reaction, including the (gamma+ gamma') at the external part of the liquid pool and the (gamma + carbide) reaction at the central part of the liquid pool. Zr inhibits the second reaction and increases the crack formation tendency, implying that it would damage the weldability of the alloy. (C) 2020 Elsevier B.V. All rights reserved. |
| WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000546685800022 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.imr.ac.cn/handle/321006/139793]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Sun, Wenru |
| 作者单位 | 1.Northeastern Univ, Sch Mat Sci & Engn, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China 2.Univ Sci & Technol Liaoning, Sch Met & Mat, Anshan 114051, Peoples R China 3.Chongqing Skyrizon Aeroengines Co Ltd, Tech Ctr, Chongqing 401135, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Qi, Feng,Yu, Lianxu,Zhao, Guangdi,et al. Effect of Zr on solidification segregation behavior of K417G alloy and its anomalous effect during rapid cooling process[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2020,835:9. |
| APA | Qi, Feng,Yu, Lianxu,Zhao, Guangdi,Xin, Xin,Zhang, Bin,&Sun, Wenru.(2020).Effect of Zr on solidification segregation behavior of K417G alloy and its anomalous effect during rapid cooling process.JOURNAL OF ALLOYS AND COMPOUNDS,835,9. |
| MLA | Qi, Feng,et al."Effect of Zr on solidification segregation behavior of K417G alloy and its anomalous effect during rapid cooling process".JOURNAL OF ALLOYS AND COMPOUNDS 835(2020):9. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。