In Situ Detection of Damage in the SiCf/Ti6242 Composite During the Thermomechanical Fatigue Test
文献类型：期刊论文
| 作者 | Kong Xu1,2; Wang Yumin1; Yang Qing1; Bian Fang1; Zhang Xu1; Zhang Guoxing1; Yang Lina1; Wu Ying1; Yang Rui1 |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2020-03-01 |
| 卷号 | 49期号:3页码:933-938 |
| 关键词 | titanium matrix composites thermomechanical fatigue acoustic emission X-ray tomography |
| ISSN号 | 1002-185X |
| 通讯作者 | Wang Yumin(yuminwang@imr.ac.cn) |
| 英文摘要 | The damage of the SiCf/Ti6242 composite in the thermomechanical fatigue test was monitored by the acoustic emission (AE) technique and the high-resolution X-ray tomography. The thermomechanical fatigue test was conducted with a trapezoidal waveform to simulate the actual loading of the bladed ring. The applied stress range was 130 similar to 1300 MPa and the temperature range was 100 similar to 500 degrees C. The maximum stress was held for 2 min at 500 degrees C. The AE events emerged mainly in the loading stage and the dwell stage for the cycle where the AE signals of fiber fracture and matrix cracking were found. The matrix cracks of the unbroken specimen were detected by the high-resolution X-ray tomography. The necking of the tungsten filament in the broken fiber in the cracking region was also found. These results show that the damage mechanism of the specimen is dominated by a mixture of fiber fracture and matrix cracking. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000551278100026 |
| 出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/139997]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang Yumin |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Kong Xu,Wang Yumin,Yang Qing,et al. In Situ Detection of Damage in the SiCf/Ti6242 Composite During the Thermomechanical Fatigue Test[J]. RARE METAL MATERIALS AND ENGINEERING,2020,49(3):933-938. |
| APA | Kong Xu.,Wang Yumin.,Yang Qing.,Bian Fang.,Zhang Xu.,...&Yang Rui.(2020).In Situ Detection of Damage in the SiCf/Ti6242 Composite During the Thermomechanical Fatigue Test.RARE METAL MATERIALS AND ENGINEERING,49(3),933-938. |
| MLA | Kong Xu,et al."In Situ Detection of Damage in the SiCf/Ti6242 Composite During the Thermomechanical Fatigue Test".RARE METAL MATERIALS AND ENGINEERING 49.3(2020):933-938. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。