Microstructure and Mechanical Properties of HSLA Steel Containing 1.4%Cu
文献类型：期刊论文
| 作者 | Du Yubin1,2; Hu Xiaofeng1; Zhang Shouqing1,2; Song Yuanyuan1; Jiang Haichang1; Rong Lijian1 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2020-10-11 |
| 卷号 | 56期号:10页码:1343-1354 |
| ISSN号 | 0412-1961 |
| 关键词 | HSLA steel Cu lath boundary element segregation impact energy |
| DOI | 10.11900/0412.1961.2020.00012 |
| 通讯作者 | Rong Lijian(ljrong@imr.ac.cn) |
| 英文摘要 | The Cu bearing high strength low alloy (HSLA) steels exhibit high-strength, high toughness and good weldability, which have been widely used in shipbuilding, offshore structures etc. Due to the extremely poor impact energy when attained peak strength, the Cu bearing HSLA steels are usually used at overaged state, which have a good combination of impact energy and strength. In order to clarify the effect of Cu on mechanical properties especially on the impact energy for HSLA steels at peak ageing state, two HSLA steels without Cu (0Cu) and with 1.4%Cu (1.4Cu), were prepared by vacuum induction melting in this study. The influence of Cu on the microstructure of HSLA steel was investigated by OM, SEM and EBSD. Meanwhile, the Cu-riched clusters were characterized by APT and the mechanical properties were measured by tensile test and impact test. The results show that the Cu is completely solid-solutioned into the matrix after quenching, and there are a great number of Cu-riched clusters precipitated in the matrix and boundaries after tempering. Cu element has no obvious effect on the prior austenite grain size, microstructure and effective grain size of tempered HSLA steel, but has significant influence on the strength and impact energy for tempered HSLA steel. After tempered at 450 degrees C, the 1.4Cu steel attained the maximum yield strength (1053 MPa), higher than that of 0Cu steel. It is worth noting that the impact energy of 1.4Cu steel tempered at 450 degrees C is only 24 J at room temperature and the impact fracture is a quasi-cleavage brittle fracture mode dominated by river patterns. However, 0Cu steel exhibits a completely ductile fracture mode dominated by dimples at room temperature and the impact energy is 127 J. The APT results show that both 0Cu and 1.4Cu tempered steels have the segregation of C, Cr, Ni, Mn elements at the lath boundary. Compared with 0Cu steel, there precipitate a great number of Cu-riched clusters at the lath boundary for 1.4Cu steel, which will result in the stress concentration and then promote the crack initiation at the lath boundary. In addition, the Cu-rich clusters precipitated at the lath boundary could prevent the Mo segregated at the lath boundary, which will decrease the bonding energy and then promote the crack propagation along the lath boundary. Besides, the negative effect of strengthening due to the Cu-riched clusters at matrix will also accelerate the crack propagation in the matrix, which will decrease the impact energy of 1.4Cu steel. Therefore, the impact energy of 1.4Cu steel is much lower than that of 0Cu steel at room temperature. |
| 资助项目 | National Key Research and Development Program of China[2016YFB0300601] ; National Key Research and Development Program of China[2017YFB1201302] ; Liaoning Revitalization Talents Program[XLYC1907143] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | SCIENCE PRESS |
| WOS记录号 | WOS:000571986900004 |
| 资助机构 | National Key Research and Development Program of China ; Liaoning Revitalization Talents Program |
| 源URL | [http://ir.imr.ac.cn/handle/321006/140690]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Rong Lijian |
| 作者单位 | 1.Chinese Acad Sci, CAS Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Du Yubin,Hu Xiaofeng,Zhang Shouqing,et al. Microstructure and Mechanical Properties of HSLA Steel Containing 1.4%Cu[J]. ACTA METALLURGICA SINICA,2020,56(10):1343-1354. |
| APA | Du Yubin,Hu Xiaofeng,Zhang Shouqing,Song Yuanyuan,Jiang Haichang,&Rong Lijian.(2020).Microstructure and Mechanical Properties of HSLA Steel Containing 1.4%Cu.ACTA METALLURGICA SINICA,56(10),1343-1354. |
| MLA | Du Yubin,et al."Microstructure and Mechanical Properties of HSLA Steel Containing 1.4%Cu".ACTA METALLURGICA SINICA 56.10(2020):1343-1354. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。