Corrosion Behaviors and Mechanisms of ODS Steel Exposed to Static Pb-Bi Eutectic at 600 and 700 degrees C
文献类型：期刊论文
| 作者 | Bao Feiyang1,2; Li Yanfen1,2,3; Wang Guangquan1,4; Zhang Jiarong1; Yan Wei1,2,3; Shi Quanqiang1,3; Shan Yiyin1,2,3; Yang Ke1,2; Xu Bin5; Song Danrong5 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2020-10-11 |
| 卷号 | 56期号:10页码:1366-1376 |
| 关键词 | advanced nuclear energy system Pb-Bi eutectic (LBE) oxide dispersion strengthened (ODS) steel high temperature corrosion oxide scale |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2020.00035 |
| 通讯作者 | Li Yanfen(yfli@imr.ac.cn) |
| 英文摘要 | With good neutron properties, anti-irradiation performances, heat transfer properties and inherent safety characteristics, liquid lead or Pb-Bi eutectic (LBE) has been a primary candidate coolant for accelerator driven system and advanced nuclear reactors. However, corrosion of structural materials is a critical challenge in the use of liquid lead and LBE in high temperature nuclear reactors. Therefore, research on corrosion compatibility of structural materials with LBE at elevated temperatures is of great significance. In this work, the long-term corrosion experiments in static LBE for a oxide dispersion strengthened (ODS) steel were carried out at 600 and 700 degrees C. The temperature effects on different corrosion behaviors were studied by the analyses of XRD, SEM and EDS, and the underlying mechanisms were clarified. After exposing to LBE at 600 degrees C for up to 2000 h, a typical double-layer oxide scale with the thickness of about 10 mu m was formed on the surface of ODS steel, which was composed of outer layers of Pb-Fe-O and Fe3O4 and inner layer of Fe-Cr-Al spinal. In addition, a thin Al-rich layer was also formed under the inner layer. Due to the protective effect of the relatively dense inner layer and the Al-rich layer, ODS steel showed excellent resistance to LBE corrosion at 600 degrees C with a significantly lower corrosion rate. On the contrary, when exposed to LBE at 700 degrees C, the structure and thickness of the oxide scale formed on the surface of the ODS steel were obviously different. After exposure for 100 h, a dense protective Al2O3 oxide layer with a thickness of about 500 nm was formed, greatly reducing the corrosion rate. With the corrosion time prolonging to 500 h at 700 degrees C, most of Al2O3 layer was still remained. However, a few of nodular-like oxides were formed originated from local weak areas, which broken off the continuity of protective Al2O3 and led to deeper corrosion by LBE. |
| 资助项目 | Nuclear Power Technology Innovation Center Project of Nuclear Power Institute of China[HDLCXZX-2019-HD-15-01] ; National Natural Science Foundation of China[U1832206] ; Institute of Metal Research, Chinese Academy of Science[JY7A7A111A1] ; Excellent Scholar Funding |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000571986900006 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | Nuclear Power Technology Innovation Center Project of Nuclear Power Institute of China ; National Natural Science Foundation of China ; Institute of Metal Research, Chinese Academy of Science ; Excellent Scholar Funding |
| 源URL | [http://ir.imr.ac.cn/handle/321006/140693]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Li Yanfen |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 4.Univ Sci & Technol China, Nano Sci & Technol Inst, Suzhou 215000, Peoples R China 5.Nucl Power Inst China, Chengdu 610005, Peoples R China |
| 推荐引用方式 GB/T 7714 | Bao Feiyang,Li Yanfen,Wang Guangquan,et al. Corrosion Behaviors and Mechanisms of ODS Steel Exposed to Static Pb-Bi Eutectic at 600 and 700 degrees C[J]. ACTA METALLURGICA SINICA,2020,56(10):1366-1376. |
| APA | Bao Feiyang.,Li Yanfen.,Wang Guangquan.,Zhang Jiarong.,Yan Wei.,...&Wei Xuedong.(2020).Corrosion Behaviors and Mechanisms of ODS Steel Exposed to Static Pb-Bi Eutectic at 600 and 700 degrees C.ACTA METALLURGICA SINICA,56(10),1366-1376. |
| MLA | Bao Feiyang,et al."Corrosion Behaviors and Mechanisms of ODS Steel Exposed to Static Pb-Bi Eutectic at 600 and 700 degrees C".ACTA METALLURGICA SINICA 56.10(2020):1366-1376. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。