Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy
文献类型:期刊论文
作者 | Sheng, L. Y.4; Du, B. N.4; Hu, Z. Y.2,4; Qiao, Y. X.1; Xiao, Z. P.1; Wang, B. J.4; Xu, D. K.3; Zheng, Y. F.4; Xi, T. F.4 |
刊名 | JOURNAL OF MAGNESIUM AND ALLOYS |
出版日期 | 2020-09-01 |
卷号 | 8期号:3页码:601-613 |
ISSN号 | 2213-9567 |
关键词 | Annealing treatment Mg-Zn-Y-Nd alloy Microstructure Tensile property |
DOI | 10.1016/j.jma.2019.07.011 |
通讯作者 | Sheng, L. Y.(lysheng@yeah.net) ; Du, B. N.(bndu10s@alum.imr.ac.cn) |
英文摘要 | In the present study, the Mg-4Zn-0.6Y-0.5Nd alloy was hot extruded and annealed at 200 degrees C, 225 degrees C and 250 degrees C for different time to optimize microstructure and mechanical properties. The results exhibit that the dual-size grain structure and linearly distributed secondary phase are the main feature of the as-extruded Mg-Zn-Y-Nd alloy, which can be described as the elongated grain is surrounded by the fine equiaxed grain. Moreover, the as-extruded alloy shows strong {01 (1) over bar0} fiber texture feature, especially for the large elongated grains. The annealing treatment results in static recrystallization, which increases fine equiaxed grains but decreases large elongated grains. In addition, the equiaxed grains formed during the annealing treatment demonstrate relative random orientations, which weaken the {01 (1) over bar0} fiber texture of the alloy. Moreover, during the annealing at 225 degrees C and 250 degrees C, the extension twins begin to form in the alloy and weaken the {01 (1) over bar0} fiber texture of the alloy further. The annealing treatment has little influence on the linearly distributed secondary phase but promotes the coarsening of small precipitates at 250 degrees C. The annealing treatment could increase the yield and ultimate strength, but the elongation decreases, especially at higher temperature. Such a variation can be ascribed to the evolution of texture, grain structure, twinning and precipitation during the annealing treatment. (c) 2020 Published by Elsevier B.V. on behalf of Chongqing University. |
资助项目 | Natural Science Foundation of Guangdong Province, China[2018A030313950] ; Shenzhen Basic Research Project[JCYJ20170815153143221] ; Shenzhen Basic Research Project[JCYJ20170815153210359] ; Shenzhen Basic Research Project[JCYJ20170306141749970] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | KEAI PUBLISHING LTD |
WOS记录号 | WOS:000571358200004 |
资助机构 | Natural Science Foundation of Guangdong Province, China ; Shenzhen Basic Research Project |
源URL | [http://ir.imr.ac.cn/handle/321006/140699] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Sheng, L. Y.; Du, B. N. |
作者单位 | 1.Jiangsu Univ Sci & Technol, Zhenjiang 212003, Jiangsu, Peoples R China 2.Shenzhen Yezhan Elect Co Ltd, Shenzhen 518110, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 4.Peking Univ, Shenzhen Inst, Shenzhen 518057, Peoples R China |
推荐引用方式 GB/T 7714 | Sheng, L. Y.,Du, B. N.,Hu, Z. Y.,et al. Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy[J]. JOURNAL OF MAGNESIUM AND ALLOYS,2020,8(3):601-613. |
APA | Sheng, L. Y..,Du, B. N..,Hu, Z. Y..,Qiao, Y. X..,Xiao, Z. P..,...&Xi, T. F..(2020).Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy.JOURNAL OF MAGNESIUM AND ALLOYS,8(3),601-613. |
MLA | Sheng, L. Y.,et al."Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy".JOURNAL OF MAGNESIUM AND ALLOYS 8.3(2020):601-613. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。