Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine
文献类型：期刊论文
| 作者 | Fan, Lei2,4; Liu, Li3; Lv, Yuhai1; Wang, Hao1; Fu, Anqing2; Yuan, Juntao2; Li, Ying4; Wang, Fuhui3; Yin, Chengxian2 |
| 刊名 | SCIENTIFIC REPORTS
 |
| 出版日期 | 2020-10-01 |
| 卷号 | 10期号:1页码:13 |
| ISSN号 | 2045-2322 |
| DOI | 10.1038/s41598-020-73034-y |
| 通讯作者 | Liu, Li(liuli@mail.neu.edu.cn) |
| 英文摘要 | The effect of pre-oxidation on the corrosion behavior of pure Ti covered with a solid NaCl deposit in the humid O-2 flow at 600 degrees C is studied. The oxide scale, formed by pre-oxidation, protects the substrate from the NaCl induced corrosion during the initial stage. However, the corrosion of the pre-oxidized sample is severely accelerated by solid NaCl after an incubation period. The chlorine, generated from the decomposition of solid NaCl, diffuses into the oxide/substrate interface as ions during the incubation period, which was observed by ToF-SIMS. The chlorine at the oxide/substrate interface induces the fast corrosion after the incubation period although the pre-oxidation scale is complete and compact. |
| 资助项目 | National Key Research and Development Program of China[2017YFF0210406] ; Shanxi National Science Foundation[2019JQ-213] ; Basic Research and Strategic Reserve Technology Research Fund (project of China National Petroleum Corporation)[2018Z-01] |
| WOS研究方向 | Science & Technology - Other Topics |
| 语种 | 英语 |
| WOS记录号 | WOS:000577143400054 |
| 出版者 | NATURE RESEARCH |
| 资助机构 | National Key Research and Development Program of China ; Shanxi National Science Foundation ; Basic Research and Strategic Reserve Technology Research Fund (project of China National Petroleum Corporation) |
| 源URL | [http://ir.imr.ac.cn/handle/321006/140920]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liu, Li |
| 作者单位 | 1.1 Gas Prod Plant Changqing Oilfield Co, Jingbian 718500, Shaanxi, Peoples R China 2.CNPC Tubular Goods Res Inst, State Key Lab Performance & Struct Safety Petr T, 89,Jinyeer Rode, Xian 710077, Shaanxi, Peoples R China 3.Northeastern Univ, Key Lab Anisotropy & Texture Mat MoE, Sch Mat Sci & Engn, 3-11,Wenhua Rd, Shenyang 110819, Peoples R China 4.Chinese Acad Sci, Inst Met Res, 62,Wencui Rd, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Fan, Lei,Liu, Li,Lv, Yuhai,et al. Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine[J]. SCIENTIFIC REPORTS,2020,10(1):13. |
| APA | Fan, Lei.,Liu, Li.,Lv, Yuhai.,Wang, Hao.,Fu, Anqing.,...&Yin, Chengxian.(2020).Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine.SCIENTIFIC REPORTS,10(1),13. |
| MLA | Fan, Lei,et al."Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine".SCIENTIFIC REPORTS 10.1(2020):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。