Cavitation erosion behavior of nitinol coating sealed by epoxy resinKavitationserosionsverhalten einer mit Epoxidharz versiegelten Nitinolbeschichtung
文献类型：期刊论文
| 作者 | Shi, Z. P.2,3; Wang, Z. B.3; Qiao, Y. X.1 |
| 刊名 | MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK
 |
| 出版日期 | 2020-11-01 |
| 卷号 | 51期号:11页码:1507-1514 |
| 关键词 | Cavitation erosion nitinol coating sealing epoxy resin air plasma spraying |
| ISSN号 | 0933-5137 |
| DOI | 10.1002/mawe.202000102 |
| 通讯作者 | Qiao, Y. X.(yxqiao@just.edu.cn) |
| 英文摘要 | The nitinol coating against cavitation erosion was prepared by air plasma spraying and sealed with epoxy resin successfully. After the coating sealed with epoxy resin, the pores and cracks of the coating were filled with the epoxy resin and then the cohesiveness between the lamellae was improved, the hardness increased from 3.68 GPa to 7.49 GPa, the energy recovery ratio (superelasticity) was improved from 41.9 % to 49.0 % and the toughness was enhanced from 0.011 GPa to 0.045 GPa. During the cavitation erosion test, the epoxy resin reduced the cavitation resources and absorbed the impact energy from the micro-jet or shock waves. Meanwhile, the high hardness and superelasticity can help the coating to resist cavitation erosion and the high toughness can delay the expansion of cracks during the cavitation erosion test. As a result, after cavitation erosion for 300 min the cumulative mass loss of the coating sealed by epoxy resin was 1/5 times as much as that of the nitinol coating without sealing. Therefore, the cavitation erosion resistance of the nitinol coating can be improved by sealed with epoxy resin. |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000587728300006 |
| 出版者 | WILEY-V C H VERLAG GMBH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/141250]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Qiao, Y. X. |
| 作者单位 | 1.Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Jiangsu, Peoples R China 2.China Acad Railway Sci, Met & Chem Res Inst, Beijing, Peoples R China 3.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Shi, Z. P.,Wang, Z. B.,Qiao, Y. X.. Cavitation erosion behavior of nitinol coating sealed by epoxy resinKavitationserosionsverhalten einer mit Epoxidharz versiegelten Nitinolbeschichtung[J]. MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK,2020,51(11):1507-1514. |
| APA | Shi, Z. P.,Wang, Z. B.,&Qiao, Y. X..(2020).Cavitation erosion behavior of nitinol coating sealed by epoxy resinKavitationserosionsverhalten einer mit Epoxidharz versiegelten Nitinolbeschichtung.MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK,51(11),1507-1514. |
| MLA | Shi, Z. P.,et al."Cavitation erosion behavior of nitinol coating sealed by epoxy resinKavitationserosionsverhalten einer mit Epoxidharz versiegelten Nitinolbeschichtung".MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK 51.11(2020):1507-1514. |