MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE
文献类型：期刊论文
| 作者 | Dong Yun2; Lin Xiaoping2; Xu Rui1; Fan Zhibin2; Ye Jie2; Wang Zhe1 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2014 |
| 卷号 | 50期号:5页码:594-600 |
| ISSN号 | 0412-1961 |
| 关键词 | ZN-Y ALLOY MECHANICAL-PROPERTIES QUASI-CRYSTAL MORPHOLOGIES BEHAVIOR RATIO Mg82.13Zn13.85Y4.02 alloy high pressure solidification stress-strain curve cleavage surface |
| 其他题名 | MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg_(82.13)Zn_(13.85)Y_(4.02) ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE |
| 英文摘要 | By the investigation of the microstructures of Mg82.13Zn13.85Y4.02 (mass fraction, %) alloy solidified under different pressure, it is found that the solidification microstructure of the alloy is consisted of alpha-Mg matrix, W-Mg3Y2Zn3 phase and I-Mg3YZn6 phase. In the microstructure of the alloy solidified under ambient pressure, the networks of the secondary phases of eutectic-like and rod-like shape are distributed in the alpha-Mg interdendritic space. As the solidification pressure increases, eutectic network is disconnected gradually and the amount of eutectic is diminished and the solubility of Zn in alpha-Mg rises gradually. The results of the measurement of the mechanical properties show that the compression strength, the yield strength and the compressibility of the alloy sample solidified under ambient pressure is 344 MPa, 331 MPa and 16% respectively. However, the compression strength, the yield strength and the compressibility of the alloy sample solidified from 1250 degrees C under 6 GPa is 455 MPa, 426 MPa and 25%, respectively. The observation of fracture surfaces shows that, in the alloy solidified under high pressure, the cleavage surface of the compressed fracture is decreased, and the tear ridge and tearing dimple can be found. The degree of cleavage fracture is decreased. |
| 资助项目 | [Natural Science Foundation of Hebei Province] ; [Natural Science Foundation of Liaoning Province] ; [Projiect of Science and Technology of Northeastern University at Qinhuangdao] |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5141014 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/141560]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Yanshan Univ, State Key Lab Metastable Materials Sci & Technol, Sch Materials Sci & Engn, Qinhuangdao 066004, Peoples R China 2.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Dong Yun,Lin Xiaoping,Xu Rui,et al. MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE[J]. ACTA METALLURGICA SINICA,2014,50(5):594-600. |
| APA | Dong Yun,Lin Xiaoping,Xu Rui,Fan Zhibin,Ye Jie,&Wang Zhe.(2014).MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE.ACTA METALLURGICA SINICA,50(5),594-600. |
| MLA | Dong Yun,et al."MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE".ACTA METALLURGICA SINICA 50.5(2014):594-600. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。