Effect of Temperature on Microstructure and Formability of Al-10 mass% Si Coatings
文献类型：期刊论文
| 作者 | Zhang Jie1; Jiang Sheming1; Zhang Qifu1; Liu Changsheng2 |
| 刊名 | JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
 |
| 出版日期 | 2016 |
| 卷号 | 23期号:3页码:270-275 |
| 关键词 | HOT SILICON STEEL Al-Si coating heating temperature microstructure formability hot-stamping |
| ISSN号 | 1006-706X |
| 其他题名 | Effect of Temperature on Microstructure and Formability of Al-10 mass%Si Coatings |
| 英文摘要 | The type-1 aluminized (Al-10 mass% Si) coating on hot stamped steel is used in commercial applications. The effect of temperature on microstructure and formability of the Al-10 mass% Si coating was investigated. Hot-dip aluminized 22MnB5 steel was heated at 870, 900, 930, and 1 050 degrees C for 5 min. After heat treatment at different temperatures, the microstructure of Al-10 mass% Si was characterized by field-emission scanning electron microscopy and energy-dispersive spectroscopy. The results show that when the Al-10 mass% Si coating was heated at 870 degrees C for 5 min, three types of intermetallic phases were formed: two ternary Fe-Si-Al phases (Fe2SiAl7+Fe2Si2Al5 and Fe2SiAl2+Fe2Si2Al5) and one binary Fe-Al phase (FeAl3). The phases in the coating became Fe2SiAl2+Fe2Si2Al5 and FeAl3, the binary Fe-Al phase near the interface became Fe2Al5 and the Si-rich layers were decreased with the increase of heating temperature. When the heat treatment was 1050 degrees C for 5 min, the Si-rich layer disappeared, the coating consisted of FeAl and Fe3Al, and the Kirkendall voids were formed. When the heating temperature was increased through 870, 900, and 930 degrees C, the coating hardness was reduced and cracks were formed in the coating after hot stamping. The formability of the coating with temperature change was confirmed by a hot stamping test. When heated at 1 050 degrees C, the coating was formable but continuous Kirkendall voids were observed. |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5660280 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/143914]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Cent Iron & Steel Res Institute, Natl Engn Lab Adv Coating Technol Met, Beijing 100081, Peoples R China 2.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Zhang Jie,Jiang Sheming,Zhang Qifu,et al. Effect of Temperature on Microstructure and Formability of Al-10 mass% Si Coatings[J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,2016,23(3):270-275. |
| APA | Zhang Jie,Jiang Sheming,Zhang Qifu,&Liu Changsheng.(2016).Effect of Temperature on Microstructure and Formability of Al-10 mass% Si Coatings.JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,23(3),270-275. |
| MLA | Zhang Jie,et al."Effect of Temperature on Microstructure and Formability of Al-10 mass% Si Coatings".JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL 23.3(2016):270-275. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。