Effect of extrusion on corrosion behavior and corrosion mechanism of Mg-Y alloy
文献类型：期刊论文
| 作者 | Xu Hong1; Zhang Xin2; Zhang Kui3; Shi Yang4; Ren Jiping1 |
| 刊名 | JOURNAL OF RARE EARTHS
 |
| 出版日期 | 2016 |
| 卷号 | 34期号:3页码:315-327 |
| 关键词 | CA ALLOYS MAGNESIUM MICROSTRUCTURE RESISTANCE AZ91D extrusion Mg-Y alloy corrosion behavior corrosion mechanism rare earths |
| ISSN号 | 1002-0721 |
| 其他题名 | Effect of extrusion on corrosion behavior and corrosion mechanism of Mg-Y alloy |
| 英文摘要 | The influences of the hot extrusion process on the microstructure, corrosion behavior and corrosion mechanism for Mg-Y magnesium alloy were studied by means of the microstructure observation, weight loss test, electrochemical test and corrosion morphology test. The results showed that with increasing of the extrusion ratio, the shear flow line on the vertical section of the extruded alloy increased, the shear bands parallel lines became more clearly visible, and a large number of fine equiaxed grains distributed in parallel with the flow lines. The open circuit potential had a certain degree of improvement after extrusion, the open circuit potential increased with increment of extrusion ratio, and the corrosion potential of the vertical section was higher than that of the same alloy in the same compression ratio. The shift rate of the corrosion potential relatively became larger with increasing of the extrusion ratio, and the cathode corrosion current corresponding to the branch migration shifted to the positive direction. The high frequency capacitive arc increased with increment of the extrusion ratio, and the radius of capacitive arc of the vertical section was slightly larger than that of the transverse section. The corrosion morphologies of Mg-0.25Y alloy were uniform corrosion, and the corrosion morphologies of Mg-(2.5, 5, 8 and 15) were the pitting corrosion and the small range, deep depth localized corrosion. |
| 资助项目 | [National Key Technology R&D Program of China] |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5655253 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/146346]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.North Univ China, Sch Materials Sci & Engn, Taiyuan 030051, Peoples R China 2.China Datang Coporat Sci & Technol Res Institute, Institute Thermal Power Generat Technol, Beijing 102206, Peoples R China 3.Gen Res Institute Nonferrous Met, State Key Lab Fabricat & Proc Nonferrous Met, Beijing 100088, Peoples R China 4.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Xu Hong,Zhang Xin,Zhang Kui,et al. Effect of extrusion on corrosion behavior and corrosion mechanism of Mg-Y alloy[J]. JOURNAL OF RARE EARTHS,2016,34(3):315-327. |
| APA | Xu Hong,Zhang Xin,Zhang Kui,Shi Yang,&Ren Jiping.(2016).Effect of extrusion on corrosion behavior and corrosion mechanism of Mg-Y alloy.JOURNAL OF RARE EARTHS,34(3),315-327. |
| MLA | Xu Hong,et al."Effect of extrusion on corrosion behavior and corrosion mechanism of Mg-Y alloy".JOURNAL OF RARE EARTHS 34.3(2016):315-327. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。