Microstructure and Mechanical Properties of Ti-Al-Zr-Cr-N Bilayer Films Deposited by Multi-arc Ion Plating
文献类型：期刊论文
| 作者 | Zhao Shilu1; Zhang Zhen2; Zhang Jun1; Wang Shuanghong1; Zhang Zhenggui1 |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2016 |
| 卷号 | 45期号:5页码:1320-1324 |
| 关键词 | COATINGS PERFORMANCE multi-arc ion plating (Ti, Al, Zr)N/(Ti, Al, Zr, Cr)N CrN/(Ti, Al, Zr, Cr)N microhardness adhesive force |
| ISSN号 | 1002-185X |
| 其他题名 | Microstructure and Mechanical Properties of Ti-Al-Zr-Cr-N Bilayer Films Deposited by Multi-arc Ion Plating |
| 英文摘要 | The (Ti, Al, Zr)N/(Ti, Al, Zr, Cr)N and CrN/(Ti, Al, Zr, Cr)N four-component bilayer nitride films were deposited on cemented carbide (WC-8%Co) substrates by a multi-arc ion plating technique using the combined Ti-Al-Zr alloy and pure Cr targets. The morphology, composition and crystalline structure of two bilayer films were analyzed by scanning electron microscopy (SEM), energy disperse X-ray spectroscopy (EDS) and X-ray diffraction (XRD). Scratch test and Vickers microindentation were used to compare the mechanical properties of the two bilayer films. It is shown that the two prepared bilayer films are still the TiN (B1-NaCl) face-centered cubic structure. The cross-sectional morphologies are typical columnar crystal structures. As the bias voltages vary from -50 to -200 V, the mechanical properties of the two bilayer films are better than those of the (Ti, Al, Zr, Cr)N monolayer films and almost close to those of the Ti-Al-Zr-Cr-N gradient films. The microhardness of the (Ti, Al, Zr)N/(Ti, Al, Zr, Cr)N bilayer film (max. HV0.01 41 GPa) is higher than that of the CrN/(Ti, Al, Zr, Cr)N film. However, the adhesive force of the CrN/(Ti, Al, Zr, Cr)N bilayer film is superior to that of the (Ti, Al, Zr)N/(Ti, Al, Zr, Cr)N film (all > 200 N). |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5713044 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/146710]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.沈阳大学 2.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Zhao Shilu,Zhang Zhen,Zhang Jun,et al. Microstructure and Mechanical Properties of Ti-Al-Zr-Cr-N Bilayer Films Deposited by Multi-arc Ion Plating[J]. RARE METAL MATERIALS AND ENGINEERING,2016,45(5):1320-1324. |
| APA | Zhao Shilu,Zhang Zhen,Zhang Jun,Wang Shuanghong,&Zhang Zhenggui.(2016).Microstructure and Mechanical Properties of Ti-Al-Zr-Cr-N Bilayer Films Deposited by Multi-arc Ion Plating.RARE METAL MATERIALS AND ENGINEERING,45(5),1320-1324. |
| MLA | Zhao Shilu,et al."Microstructure and Mechanical Properties of Ti-Al-Zr-Cr-N Bilayer Films Deposited by Multi-arc Ion Plating".RARE METAL MATERIALS AND ENGINEERING 45.5(2016):1320-1324. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。