Improving friction stir weldability of Al/Mg alloys via ultrasonically diminishing pin adhesion
文献类型：期刊论文
| 作者 | Meng Xiangchen1; Jin Yanye1; Ji Shude1; Yan Dejun2 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2018 |
| 卷号 | 34期号:10页码:1817-1822 |
| 关键词 | MECHANICAL-PROPERTIES ALUMINUM-ALLOY MAGNESIUM ALLOY INTERMETALLIC COMPOUNDS MG ALLOYS AL-ALLOY SHOULDER MICROSTRUCTURE EVOLUTION JOINTS Friction stir welding Ultrasonic Aluminum/magnesium alloys Pin adhesion Intermetallic compounds Stationary shoulder |
| ISSN号 | 1005-0302 |
| 英文摘要 | Formation of intermetallic compounds (IMCs) during friction stir welding (FSW) of aluminum/magnesium (Al/Mg) alloys easily results in the pin adhesion and then deteriorates joint formation. The severe pin adhesion transformed the tapered-and-screwed pin into a tapered pin at a low welding speed of 30 mm/min. The pin adhesion problem was solved with the help of ultrasonic. The weldability of Al/Mg alloys was significantly improved due to the good material flow induced by mechanical vibration and the fragments of the IMCs on the surface of a rotating pin caused by acoustic streaming, respectively. A sound joint with ultrasonic contained long Al/Mg interface joining length and complex mixture of Al/Mg alloys in the stir zone, thereby achieving perfect metallurgical bonding and mechanical interlocking. The ultrasonic could broaden process window and then improve tensile properties. The tensile strength of the Al/Mg joint with ultrasonic reached 115 MPa. (C) 2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 资助项目 | [National Natural Science Foundation of China] ; [Program for Liaoning ExcellentTalents in University] ; [China PostdoctoralScience Foundation] ; [Guangdong Provincial Key Laboratory of Advanced Welding Technology] |
| 语种 | 英语 |
| CSCD记录号 | CSCD:6335112 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/146768]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.中国科学院金属研究所 2.中国科学院广州地球化学研究所 |
| 推荐引用方式 GB/T 7714 | Meng Xiangchen,Jin Yanye,Ji Shude,et al. Improving friction stir weldability of Al/Mg alloys via ultrasonically diminishing pin adhesion[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2018,34(10):1817-1822. |
| APA | Meng Xiangchen,Jin Yanye,Ji Shude,&Yan Dejun.(2018).Improving friction stir weldability of Al/Mg alloys via ultrasonically diminishing pin adhesion.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,34(10),1817-1822. |
| MLA | Meng Xiangchen,et al."Improving friction stir weldability of Al/Mg alloys via ultrasonically diminishing pin adhesion".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 34.10(2018):1817-1822. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。