Effect of squeeze casting process on microstructures and flow stress behavior of Al-17. 5Si-4Cu-0. 5Mg alloy
文献类型：期刊论文
| 作者 | Shi Yuanji; Liu Lanji; Zhang Lei; Zhang Lijun; Zheng Li; Li Runxia; Yu Baoyi |
| 刊名 | JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
 |
| 出版日期 | 2017 |
| 卷号 | 24期号:9页码:957-965 |
| ISSN号 | 1006-706X |
| 关键词 | MECHANICAL-PROPERTIES CONSTITUTIVE-EQUATIONS ALUMINUM-ALLOY STRAIN-RATE AL-ALLOY TEMPERATURE PARTICLES STEEL Squeeze casting Al-Si-Cu-Mg alloy Hot compression deformation Flow stress Constitutive equation |
| 其他题名 | Effect of squeeze casting process on microstructures and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy |
| 英文摘要 | The effects of squeeze casting process on microstructure and flow stress behavior of Al-17. 5Si-4Cu-0.5Mg alloy were investigated and the hot-compression tests of gravity casting and squeeze casting alloy were carried out at 350-500 degrees C and 0. 001-5 s(-1). The results show that microstructures of Al-17. 5Si-4Cu-0. 5Mg alloys were obviously improved by squeeze casting. Due to the decrease of coarse primary Si particles, soft alpha-Al dendrite as well as the fine microstructures appeared, and the mechanical properties of squeeze casting alloys were improved. However, when the strain rate rises or the deformation temperature decreases, the flow stress increases and it was proved that the alloy is a positive strain rate sensitive material. It was deduced that compared with the gravity casting alloy, squeeze casting alloy (solidified at 632 MPa) is more difficult to deform since the flow stress of squeeze casting alloy is higher than that of gravity casting alloy when the deformation temperature exceeds 400 degrees C. Flow stress behavior of Al-17. 5Si-4Cu-0. 5Mg alloy can he described by a hyperbolic sine form with Zener-Hollomon parameter, and the average hot deformation activation energy Q of gravity casting alloy and squeeze casting alloy is 278. 97 and 308. 77 kJ/mol, respectively. |
| 资助项目 | [National Natural Science Foundation of China] ; [Shenyang City Application Basic Research Foundation] |
| 语种 | 英语 |
| CSCD记录号 | CSCD:6077477 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/148410]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Shi Yuanji,Liu Lanji,Zhang Lei,et al. Effect of squeeze casting process on microstructures and flow stress behavior of Al-17. 5Si-4Cu-0. 5Mg alloy[J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,2017,24(9):957-965. |
| APA | Shi Yuanji.,Liu Lanji.,Zhang Lei.,Zhang Lijun.,Zheng Li.,...&Yu Baoyi.(2017).Effect of squeeze casting process on microstructures and flow stress behavior of Al-17. 5Si-4Cu-0. 5Mg alloy.JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,24(9),957-965. |
| MLA | Shi Yuanji,et al."Effect of squeeze casting process on microstructures and flow stress behavior of Al-17. 5Si-4Cu-0. 5Mg alloy".JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL 24.9(2017):957-965. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。