High Temperature Oxidation Resistance of Ti-Al-Zr-Cr-N Composite Films on Cemented Carbide Substrates
文献类型：期刊论文
| 作者 | Zhao Shilu; Zhang Jun; Chen Weihua; Wang Shuanghong |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2014 |
| 卷号 | 43期号:2页码:341-345 |
| 关键词 | MECHANICAL-PROPERTIES COATINGS DEPOSITION (Ti, Al, Zr, Cr) N monolayer film TiAlZrCr/(Ti, Al, Zr, Cr) N gradient film multi-arc ion plating cemented carbide high temperature oxidation resistance |
| ISSN号 | 1002-185X |
| 其他题名 | High Temperature Oxidation Resistance of Ti-Al-Zr-Cr-N Composite Films on Cemented Carbide Substrates |
| 英文摘要 | The (Ti, Al, Zr, Cr) N monolayer and TiAlZrCr/(Ti, Al, Zr, Cr) N gradient films were deposited on cemented carbide (WC-8%Co) substrates by multi-arc ion plating technique using the combined Ti-Al-Zr alloy and pure Cr targets. Short-term isothermal (at 600, 700, 800 and 900 degrees C for 4 h) and long-term cyclic (at 600 and 700 degrees C for 100 h) oxidation tests of the two films were carried out. And the oxide scales formed on the film specimens were characterized by SEM and XRD. Results show that under short-term isothermal condition, the high temperature oxidation resistances are excellent for both the (Ti, Al, Zr, Cr) N monolayer films (up to 700 degrees C) and the TiAlZrCr/(Ti, Al, Zr, Cr) N gradient films (up to 800 degrees C). On the other hand, under long-term cyclic condition, the oxidation resistant temperatures of the (Ti, Al, Zr, Cr) N monolayer and TiAlZrCr/(Ti, Al, Zr, Cr) N gradient films are 600 and 700 degrees C, respectively. |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5070805 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/148492]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Zhao Shilu,Zhang Jun,Chen Weihua,et al. High Temperature Oxidation Resistance of Ti-Al-Zr-Cr-N Composite Films on Cemented Carbide Substrates[J]. RARE METAL MATERIALS AND ENGINEERING,2014,43(2):341-345. |
| APA | Zhao Shilu,Zhang Jun,Chen Weihua,&Wang Shuanghong.(2014).High Temperature Oxidation Resistance of Ti-Al-Zr-Cr-N Composite Films on Cemented Carbide Substrates.RARE METAL MATERIALS AND ENGINEERING,43(2),341-345. |
| MLA | Zhao Shilu,et al."High Temperature Oxidation Resistance of Ti-Al-Zr-Cr-N Composite Films on Cemented Carbide Substrates".RARE METAL MATERIALS AND ENGINEERING 43.2(2014):341-345. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。