Analysis on the rule of soft reduction gradient for continuous casting slab of different steel grades
文献类型：期刊论文
| 作者 | Lin Qiyong; Zhu Miaoyong |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2007 |
| 卷号 | 43期号:12页码:1297-1300 |
| 关键词 | continuous casting slab soft reduction reduction gradient reduction rate |
| ISSN号 | 0412-1961 |
| 其他题名 | ANALYSIS ON THE RULE OF SOFT REDUCTION GRADIENT FOR CONTINUOUS CASTING SLAB OF DIFFERENT STEEL GRADES |
| 英文摘要 | Based on the theoretical model of soft reduction gradient, the soft reduction gradients for continuous casting slabs with different steel grades were investigated. The results show that there are no big changes of the range of soft reduction gradient and soft reduction rate for casting steel grades, such as low carbon, low carbon peritectic, peritectic and medium carbon, which changed from 0.26 to 0.16 mm/m and 0.37 to 0.22 mm/min, respectively. The average soft reduction gradient and average soft reduction rate almost have no change as the steel grade changed, which keep 0.21 mm/m and 0.29 mm/min, respectively. It also can be concluded that the soft reduction amount was influenced by steel grade greatly, and it became larger with the increase of the range between liquidus temperature and solidus temperature. |
| 语种 | 英语 |
| CSCD记录号 | CSCD:3045946 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/152554]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Lin Qiyong,Zhu Miaoyong. Analysis on the rule of soft reduction gradient for continuous casting slab of different steel grades[J]. ACTA METALLURGICA SINICA,2007,43(12):1297-1300. |
| APA | Lin Qiyong,&Zhu Miaoyong.(2007).Analysis on the rule of soft reduction gradient for continuous casting slab of different steel grades.ACTA METALLURGICA SINICA,43(12),1297-1300. |
| MLA | Lin Qiyong,et al."Analysis on the rule of soft reduction gradient for continuous casting slab of different steel grades".ACTA METALLURGICA SINICA 43.12(2007):1297-1300. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。