MICROSTRUCTURE EVOLUTION AND MECHANICAL PROPERTIES OF DD5 SINGLE CRYSTAL SUPERALLOY JOINT BRAZED BY Co-BASED FILLER ALLOY
文献类型：期刊论文
| 作者 | Sun Yuan2; Liu Jide2; Liu Zhongming1; Yang Jinxia2; Li Jinguo2; Jin Tao2; Sun Xiaofeng2 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2013 |
| 卷号 | 49期号:12页码:1581-1589 |
| 关键词 | brazing single crystal superalloy Co-based filler alloy microstructure mechanical properties |
| ISSN号 | 0412-1961 |
| 其他题名 | MICROSTRUCTURE EVOLUTION AND MECHANICAL PROPERTIES OF DD5 SINGLE CRYSTAL SUPERALLOY JOINT BRAZED BY Co—BASED FILLER ALLOY |
| 英文摘要 | The single crystal supperalloy DD5 was brazed using Co-Ni-Si-B filler alloy at 1453 K. The microstructure of joint and effect of brazing time on the microstructure and mechanical properties were investigated by SEM, EPMA and TEM. The formation mechanism of joint was discussed deeply. The result indicates that three distinct regions can be identified in a joint: the filler alloy zone, interfacial bonding zone, element diffusion zone. The filler alloy zone in the center of joint consists of Ni-Co solid solution, M3B2-type boride, CrB and Ni-Si compounds. The interfacial bonding zone adjacent to the filler alloy zone is composed of Ni-Co solid solution formed isothermally at brazing temperature. The element diffusion zone between the interfacial bonding zone and substrate consists of gamma phase, gamma' phase and granular M3B2 phase which was formed in element diffusion. With extending brazing time, the brazing defects reduce, the thickness of bonding layer and the size of spherical Ni-Co solid solution in the filler alloy zone increase, and the brittle compounds reduce. The tensile strength at 1143 K increases from 198.5 MPa to 580 MPa. The investigation on fracture of high temperature tensile specimens exhibits that the fracture occurred in the seam and the fractural model is a mixed fracture. Through extending brazing time the bonding strength between seam and substrate can be improved, the brittle compounds can be controlled and the mechanical properties of joint are improved. The analysis results of microstructure and properties also imply that the optimum holding time would be 180 min. |
| 资助项目 | [National Basic Research Program of China] ; [National Natural Science Foundation of China] |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5025730 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/153515]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.中国科学院金属研究所 2.中国科学院 |
| 推荐引用方式 GB/T 7714 | Sun Yuan,Liu Jide,Liu Zhongming,et al. MICROSTRUCTURE EVOLUTION AND MECHANICAL PROPERTIES OF DD5 SINGLE CRYSTAL SUPERALLOY JOINT BRAZED BY Co-BASED FILLER ALLOY[J]. ACTA METALLURGICA SINICA,2013,49(12):1581-1589. |
| APA | Sun Yuan.,Liu Jide.,Liu Zhongming.,Yang Jinxia.,Li Jinguo.,...&Sun Xiaofeng.(2013).MICROSTRUCTURE EVOLUTION AND MECHANICAL PROPERTIES OF DD5 SINGLE CRYSTAL SUPERALLOY JOINT BRAZED BY Co-BASED FILLER ALLOY.ACTA METALLURGICA SINICA,49(12),1581-1589. |
| MLA | Sun Yuan,et al."MICROSTRUCTURE EVOLUTION AND MECHANICAL PROPERTIES OF DD5 SINGLE CRYSTAL SUPERALLOY JOINT BRAZED BY Co-BASED FILLER ALLOY".ACTA METALLURGICA SINICA 49.12(2013):1581-1589. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。