Microstructural evolution of a nickel-base single-crystal superalloy during high-temperature homogenisation
文献类型：期刊论文
| 作者 | Li, Xiangwei; Ding, Rengen; Wen, Donghui; Wang, Yao; Chu, Mingqiang; Wang, Li; Zhang, Peng; Zhang, Shuyan |
| 刊名 | MATERIALS SCIENCE AND TECHNOLOGY
 |
| 出版日期 | 2020-12-04 |
| DOI | 10.1080/02670836.2020.1852514 |
| 英文摘要 | Microstructural evolution of a nickel-base single-crystal superalloy during homogenisation at ultra-high temperature has been investigated using scanning electron microscope and electron probe microanalyzer. The results show that incipient melting occurs and all gamma/gamma ' eutectics are re-melted into liquid after 1 h homogenisation at 1350 degrees C. The volume fraction of IM decreases gradually with increasing homogenisation time. The IM disappears totally after 14 h homogenisation. Moreover, the formation of the TCP phase is suppressed during long-term thermal exposure at 1100 degrees C for the reduction of element segregation, especially the segregation of refractory element Re was reduced during ultra-high-temperature homogenisation. The microstructure evolution of IM was discussed based on the element diffusion during homogenisation. |
| WOS记录号 | WOS:000596217800001 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/155648]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Li, Xiangwei,Ding, Rengen,Wen, Donghui,et al. Microstructural evolution of a nickel-base single-crystal superalloy during high-temperature homogenisation[J]. MATERIALS SCIENCE AND TECHNOLOGY,2020. |
| APA | Li, Xiangwei.,Ding, Rengen.,Wen, Donghui.,Wang, Yao.,Chu, Mingqiang.,...&Zhang, Shuyan.(2020).Microstructural evolution of a nickel-base single-crystal superalloy during high-temperature homogenisation.MATERIALS SCIENCE AND TECHNOLOGY. |
| MLA | Li, Xiangwei,et al."Microstructural evolution of a nickel-base single-crystal superalloy during high-temperature homogenisation".MATERIALS SCIENCE AND TECHNOLOGY (2020). |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。