The corrosion behavior of Ni-Cr-Al alloys exposed to mixed oxidizing- carburizing atmospheres at 800 degrees C
文献类型：期刊论文
| 作者 | Guo, X. H.; Shen, J.; Liu, S.; Chen, J.; Niu, Y. |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2020-11-01 |
| 卷号 | 176 |
| DOI | 10.1016/j.corsci.2020.108877 |
| 英文摘要 | Ni-10/15Cr-7Al and Ni-5Cr-10Al (at.%) were exposed at 800 degrees C to three C/O gas mixtures: two (Gases 1,2) could oxidize both chromium and aluminum, while the third gas (Gas 3) only aluminum. Ni-5Cr-10Al formed always alumina scales. Reaction of Ni-10/15Cr-7Al with Gases 1 and 2 formed external chromia plus internal alumina, while Gas 3 produced external alumina plus internal chromium carbides. The external alumina growth on Ni-10/15Cr-7Al in Gas 3 is attributed to a reduced critical aluminum content for internal-to-external oxidation with respect to Gases 1 and 2. Oxidation maps are used to interpret the results in Gases 1 and 2. |
| WOS记录号 | WOS:000595991600004 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/155661]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Guo, X. H.,Shen, J.,Liu, S.,et al. The corrosion behavior of Ni-Cr-Al alloys exposed to mixed oxidizing- carburizing atmospheres at 800 degrees C[J]. CORROSION SCIENCE,2020,176. |
| APA | Guo, X. H.,Shen, J.,Liu, S.,Chen, J.,&Niu, Y..(2020).The corrosion behavior of Ni-Cr-Al alloys exposed to mixed oxidizing- carburizing atmospheres at 800 degrees C.CORROSION SCIENCE,176. |
| MLA | Guo, X. H.,et al."The corrosion behavior of Ni-Cr-Al alloys exposed to mixed oxidizing- carburizing atmospheres at 800 degrees C".CORROSION SCIENCE 176(2020). |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。