Austempering of hot rolled transformation-induced plasticity steels
文献类型：期刊论文
| 作者 | Li Zhuang2; Wu Di1 |
| 刊名 | JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING
 |
| 出版日期 | 2008 |
| 卷号 | 15期号:2页码:143-149 |
| 关键词 | MN TRIP STEELS MECHANICAL-PROPERTIES RETAINED AUSTENITE MICROSTRUCTURE SI DEFORMATION ADDITIONS austempering hot rolling transformation induced plasticity mechanical properties |
| ISSN号 | 1005-8850 |
| 其他题名 | Austempering of hot rolled transformation-induced plasticity steels |
| 英文摘要 | Thermomechanical controlled processing (TMCP) was conducted by using a laboratory hot rolling mill. Austempering in the salt bath after hot rolling was investigated. The effect of isothermal holding time on mechanical properties was studied through examining of the microstructure and mechanical properties of the specimens. The mechanism of transformation-induced plasticity (TRIP) was discussed. The results show that the microstructure of these steels consists of polygonal ferrite, granular bainite, and a significant amount of stable retained austenite. Strain-induced transformation to martensite of retained austenite and TRIP occur in the hot rolled Si-Mn TRIP steels. Excellent mechanical properties were obtained for various durations at 400 degrees C. Prolonged holding led to cementite precipitation, which destabilized the austenite. The mechanical properties were optimal when the specimen was held for 25 min, and the tensile strength, total elongation, and strength ductility balance reached the maximum values of 776 MPa, 33%, and 25608 MPa.%, respectively. (c) 2008 University of Science and Technology Beijing. All rights reserved. |
| 语种 | 英语 |
| CSCD记录号 | CSCD:3316385 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/156240]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.东北大学 2.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Li Zhuang,Wu Di. Austempering of hot rolled transformation-induced plasticity steels[J]. JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING,2008,15(2):143-149. |
| APA | Li Zhuang,&Wu Di.(2008).Austempering of hot rolled transformation-induced plasticity steels.JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING,15(2),143-149. |
| MLA | Li Zhuang,et al."Austempering of hot rolled transformation-induced plasticity steels".JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING 15.2(2008):143-149. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。