Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone
文献类型：期刊论文
| 作者 | Ming Hongliang2; Zhang Zhiming2; Xiu Pengyuan2; Wang Jianqiu2; Han Enhou2; Ke Wei2; Su Mingxing1 |
| 刊名 | Acta Metallurgica Sinica(English Letters)
 |
| 出版日期 | 2016 |
| 卷号 | 29期号:9页码:848-858 |
| 关键词 | Austenitic stainless steels Heat-affected zone Microstructure EBSD Residual strain Stress corrosion cracking |
| ISSN号 | 1006-7191 |
| 其他题名 | Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone |
| 英文摘要 | Austenitic stainless steels are usually chosen to make many components of nuclear power plants (NPPs). However, their microstructure in the heat-affected zone (HAZ) will change during the welding process. Some failures of the weld joints, mainly stress corrosion cracking (SCC), have been found to be located in the HAZ. In this research, the microstructure, micro-hardness, residual strain and SCC behavior at different locations of the 316L HAZ cut from a safeend dissimilar metal weld joint were studied. However, traditional optical microscope observation could not find any microstructural difference between the HAZ and the base metal, higher residual strain and micro-hardness, and higher fraction of random high-angle grain boundaries were found in the HAZ than in the base metal when studied by using electron back-scattering diffraction scanning and micro-hardness test. What's more, the residual strain, the microhardness and the fraction of random grain boundaries decreased, while the fraction of coincidence site lattice grain boundaries increased with increasing the distance from the fusion boundary in 316L HAZ. Creviced bent beam test was applied to evaluate the SCC susceptibility at different locations of 316L HAZ and base metal. It was found that the HAZ had higher SCC susceptibility than the base metal and SCC resistance increased when increasing the distance from the fusion boundary in 316L HAZ. |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5804838 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/156354]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Shanghai Research Center for Weld and Detection Engineering Technique of Nuclear Equipment 2.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Ming Hongliang,Zhang Zhiming,Xiu Pengyuan,et al. Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone[J]. Acta Metallurgica Sinica(English Letters),2016,29(9):848-858. |
| APA | Ming Hongliang.,Zhang Zhiming.,Xiu Pengyuan.,Wang Jianqiu.,Han Enhou.,...&Su Mingxing.(2016).Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone.Acta Metallurgica Sinica(English Letters),29(9),848-858. |
| MLA | Ming Hongliang,et al."Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone".Acta Metallurgica Sinica(English Letters) 29.9(2016):848-858. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。