Hot Deformation Behavior of an Ultra-High-Strength Fe–Ni–Co-Based Maraging Steel
文献类型：期刊论文
| 作者 | Zhang Le; Wang Wei; Babar Shahzad M; Shan Yiyin; Yang Ke |
| 刊名 | Acta Metallurgica Sinica(English Letters)
 |
| 出版日期 | 2019 |
| 卷号 | 32期号:9页码:1161-1172 |
| 关键词 | Maraging steel Hot working Dynamic recrystallization Constitutive equation Hot processing map |
| ISSN号 | 1006-7191 |
| 其他题名 | Hot Deformation Behavior of an Ultra-High-Strength Fe–Ni–Co-Based Maraging Steel |
| 英文摘要 | Hot processing behavior of an ultra-high-strength Fe–Ni–Co-based maraging steel was studied in temperature range of 900–1200 °C and strain rate range of 0.001–10 s~(–1). Deformation processing parameters and optimum hot working window were characterized via flow stress analysis, constitutive equation construction, hot processing map calculation and microstructure evolution, respectively. Critical strain value for dynamic recrystallization was determined through theoretical mathematical differential method: the inflection point of θ–σ and – ?θ/?σ – σ curves. It was found that the flow stress increased with the decrease in deformation temperature and increase in the strain rate. The power dissipation maps in the strain range of 0.1–0.6 were entirely similar with the tendency of contour lines which implied that strain had no strong effect on the dissipation maps. Nevertheless, the instability maps showed obvious strain sensitivity with increasing strain, which was ascribed to the flow localization and instability. The optimized hot processing window of the experimental steel was obtained as 1100–1200 °C/0.001~(–1) s–1 and 1000–1100 °C/0.001–0.1 s~(–1), with the efficiency range of 20–40%. Owing to high Mo content in the experimental steel, high dynamic activation energy, Q = 439.311 kJ mol~(–1), was achieved, indicating that dynamic recrystallization was difficult to occur in the hot deformation process, which was proved via microstructure analysis under different hot deformation conditions. |
| 语种 | 英语 |
| CSCD记录号 | CSCD:6563720 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/156991]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Zhang Le,Wang Wei,Babar Shahzad M,et al. Hot Deformation Behavior of an Ultra-High-Strength Fe–Ni–Co-Based Maraging Steel[J]. Acta Metallurgica Sinica(English Letters),2019,32(9):1161-1172. |
| APA | Zhang Le,Wang Wei,Babar Shahzad M,Shan Yiyin,&Yang Ke.(2019).Hot Deformation Behavior of an Ultra-High-Strength Fe–Ni–Co-Based Maraging Steel.Acta Metallurgica Sinica(English Letters),32(9),1161-1172. |
| MLA | Zhang Le,et al."Hot Deformation Behavior of an Ultra-High-Strength Fe–Ni–Co-Based Maraging Steel".Acta Metallurgica Sinica(English Letters) 32.9(2019):1161-1172. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。