Effect of Bi addition on the shear strength and failure mechanism of low-Ag lead-free solder joints
文献类型：期刊论文
| 作者 | Chen, Yinbo1,2; Meng, Zhi-Chao1,2; Gao, Li-Yin3; Liu, Zhi-Quan1,3 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
 |
| 出版日期 | 2021 |
| 页码 | 15 |
| ISSN号 | 0957-4522 |
| DOI | 10.1007/s10854-020-04982-4 |
| 通讯作者 | Liu, Zhi-Quan(zqliu@siat.ac.cn) |
| 英文摘要 | To optimize the mechanical properties of low-Ag lead-free solder, different amount of Bi element was added into the Sn-1.0Ag-0.5Cu (SAC105) to form SAC105-xBi (0 <= x <= 4) solder alloy. The microstructural evolution and shear fracture of SAC105-xBi solder joints were systematically investigated to clarify the failure mechanism after reflow and after 175 degrees C aging compared to SAC305. It was found that Bi element could provide solution strengthening and second-phase strengthening in the low-Ag SAC solder joints depending on the amount of added Bi element. The shear strength after reflow increased from 34.79 to 70.16 MPa with the increase of Bi addition from x = 0.0 to x = 4.0, while that after aging at 175 degrees C for 168 h increased from 28.97 MPa (x = 0.0) to 55.02 MPa (x = 4.0). The thickness of IMC decreased with the addition of Bi, and excessive Bi would precipitate in the matrix when the Bi content reached 2 wt% or even form brittle Bi barrier layer after 4 wt% addition. During shear tests, three kinds of fracture mode including ductile fracture, quasi-cleavage fracture, and cleavage brittle fracture were observed, and three kinds of failure position including solder matrix, Cu6Sn5/solder interface, and Cu3Sn/Cu interface were revealed. The failure mechanism of different solder joints was closely related to the coupling effects among the Bi amount in the matrix, the thicknesses of IMC, and the status of Kirkendall voids, which significantly affected the reliability of SAC solder joints. Finally, SAC105-1.0Bi solder alloy was considered having the most suitable Bi addition with anticipated comprehensive properties compared with SAC305. |
| 资助项目 | National Key R&D Program of China[2017YFB0305700] |
| WOS研究方向 | Engineering ; Materials Science ; Physics |
| 语种 | 英语 |
| WOS记录号 | WOS:000604092100027 |
| 出版者 | SPRINGER |
| 资助机构 | National Key R&D Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/158936]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liu, Zhi-Quan |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Shenzhen Inst Adv Elect Mat, Shenzhen Inst Adv Technol, Shenzhen 518055, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen, Yinbo,Meng, Zhi-Chao,Gao, Li-Yin,et al. Effect of Bi addition on the shear strength and failure mechanism of low-Ag lead-free solder joints[J]. JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS,2021:15. |
| APA | Chen, Yinbo,Meng, Zhi-Chao,Gao, Li-Yin,&Liu, Zhi-Quan.(2021).Effect of Bi addition on the shear strength and failure mechanism of low-Ag lead-free solder joints.JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS,15. |
| MLA | Chen, Yinbo,et al."Effect of Bi addition on the shear strength and failure mechanism of low-Ag lead-free solder joints".JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS (2021):15. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。