Effect of microstructure on the adhesion strength of TiBx coating on Ti6Al4V substrate
文献类型:期刊论文
作者 | Wu, Bi1,2; Gao, Siyang1; Xue, Weihai1; Li, Shu1; Duan, Deli1,2 |
刊名 | CERAMICS INTERNATIONAL |
出版日期 | 2021-02-15 |
卷号 | 47期号:4页码:5019-5027 |
ISSN号 | 0272-8842 |
关键词 | Titanium diboride Magnetron sputtering Microstructure Adhesion strength High-speed rubbing |
DOI | 10.1016/j.ceramint.2020.10.078 |
通讯作者 | Gao, Siyang(Sygao@imr.ac.cn) ; Duan, Deli(Duandl@imr.ac.cn) |
英文摘要 | TiBx coatings were deposited on Ti6Al4V and Si (100) wafer substrates by D.C. magnetron sputtering with various target-to-substrate distances (T.S. distances) from 50 mm to 200 mm. The influence of T.S. distance on the microstructure, hardness and adhesion strength of TiBx coatings and Ti6Al4V substrate system was investigated. Results showed that the microstructure of TiBx coatings transformed from dense to fibre columnar grain with the increase in T.S. distance, whilst the hardness decreased from 20.9 GPa to 9.4 GPa. The Rockwell-C indentation adhesion strength grade was also improved from HF6 to HF1. An adhesion evaluation factor G, which is related to the mechanical properties and the microstructure of TiBx coating, is proposed based on the test results. The adhesion strength increased with G, which corresponded well with the results of indentation test. The high-speed rubbing test with a sliding speed of 300 m/s was performed to check the Al-adhesion resistance of the TiBx coating against Al-hBN seal coating. |
资助项目 | National Natural Science Foundation of China[50675215] ; Tribology Science Fund of Shenyang Key Laboratory of Aero-engine Material Tribology[SKLAMT201801] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000608700100002 |
资助机构 | National Natural Science Foundation of China ; Tribology Science Fund of Shenyang Key Laboratory of Aero-engine Material Tribology |
源URL | [http://ir.imr.ac.cn/handle/321006/159041] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Gao, Siyang; Duan, Deli |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Wu, Bi,Gao, Siyang,Xue, Weihai,et al. Effect of microstructure on the adhesion strength of TiBx coating on Ti6Al4V substrate[J]. CERAMICS INTERNATIONAL,2021,47(4):5019-5027. |
APA | Wu, Bi,Gao, Siyang,Xue, Weihai,Li, Shu,&Duan, Deli.(2021).Effect of microstructure on the adhesion strength of TiBx coating on Ti6Al4V substrate.CERAMICS INTERNATIONAL,47(4),5019-5027. |
MLA | Wu, Bi,et al."Effect of microstructure on the adhesion strength of TiBx coating on Ti6Al4V substrate".CERAMICS INTERNATIONAL 47.4(2021):5019-5027. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。