Low-Temperature Molten Salt Synthesis and Characterization of Nanowire-Like TaB2 Powder

文献类型：期刊论文

作者Shah, Liaqat Ali
刊名JOM
出版日期2021-01-04
页码7
ISSN号1047-4838
DOI10.1007/s11837-020-04509-6
英文摘要TaB2 nanopowder has been prepared by the molten salt synthesis (MSS) technique. Nanowire-like TaB2 nanopowder was successfully synthesized by reacting in the Ta2O5-MgB2 system using KCl/NaCl as reaction media. The impact of the firing temperature (800 degrees C to 1000 degrees C), firing time (1 h to 4 h), and ratio of reactants to salt (1:0, 1:2, 1:5, and 1:10) on the preparation of the TaB2 nanopowder was examined. The resultant powder samples were characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD) analysis, transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), and surface area analysis (SAA). The results showed that the reaction involved in the formation of crystalline TaB2 nanopowder could be completed successfully at 1000 degrees C after 4 h of firing when the mass ratio of reactants to salt was 1:5. The resulting TaB2 nanopowders exhibited nanowire-like morphology.
WOS关键词ZRB2 POWDERS ; COMPOSITES ; CERAMICS
资助项目Chinese Academy of Sciences under the President's International Support Initiative (PIFI)[2017PE0006]
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering ; Mineralogy ; Mining & Mineral Processing
语种英语
WOS记录号WOS:000604800800001
出版者SPRINGER
资助机构Chinese Academy of Sciences under the President's International Support Initiative (PIFI)
源URL[http://ir.ipe.ac.cn/handle/122111/43082]  
专题中国科学院过程工程研究所
通讯作者Shah, Liaqat Ali
作者单位Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Beijing, Peoples R China
推荐引用方式
GB/T 7714		 Shah, Liaqat Ali. Low-Temperature Molten Salt Synthesis and Characterization of Nanowire-Like TaB2 Powder[J]. JOM,2021:7.
APA Shah, Liaqat Ali.(2021).Low-Temperature Molten Salt Synthesis and Characterization of Nanowire-Like TaB2 Powder.JOM,7.
MLA Shah, Liaqat Ali."Low-Temperature Molten Salt Synthesis and Characterization of Nanowire-Like TaB2 Powder".JOM (2021):7.

入库方式： OAI收割

来源：过程工程研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。