Hydrothermal synthesis of boehmites with various particle sizes and transition to α-Al2O3 powders by calcination
文献类型：期刊论文
| 作者 | Hu P(胡鹏) ; Hu P(胡鹏); Hu P(胡鹏)
|
| 刊名 | 广东有色金属学报
 |
| 出版日期 | 2005 |
| 卷号 | 15.0期号:002页码:581 |
| 关键词 | 热液合成 一水软铝石 粒子结构 粉末 结构材料 |
| ISSN号 | 1003-7837 |
| 英文摘要 | Boehmite powders with various particle sizes have becn prepared by hydrothermal method and the α-Al2O3 powders yieldcd after subsequent calcination have been studied, Dispersive crystalline boehmite powders of 30-100 nm, 0, 4-0, 6μm and 1μm in size were obtained respectively by changing the hydrothermal precursors and the pH value of hydrothermal slurry. Calcination of boehmite powders of 30-100 nm at 1250℃ for lh resulted in the formation of single phase α-Al2O3, and the products consisted of vermicular particles. The boehmite powders of 0.4-0, 6μm were also fully converted to α-Al2O3 at 1250℃, and the products consisted of plate-like particles with the same size of 0, 4-0, 6μm, The boehmite powders of 1μm calcined at 1350℃ for 2h were still composed of a little proportions of transition aluminas besides α-Al2O3, and the particles sitiered severely. The reaction processes for the formation of crystalline boehmites under hydrothermal conditions and α-Al2O3 powders during calcination have been discussed. |
| 语种 | 英语 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/47302]  |
| 专题 | 中国科学院过程工程研究所 |
| 作者单位 | 中国科学院过程工程研究所 |
| 推荐引用方式 GB/T 7714 | Hu P,Hu P,Hu P. Hydrothermal synthesis of boehmites with various particle sizes and transition to α-Al2O3 powders by calcination[J]. 广东有色金属学报,2005,15.0(002):581. |
| APA | 胡鹏,胡鹏,&胡鹏.(2005).Hydrothermal synthesis of boehmites with various particle sizes and transition to α-Al2O3 powders by calcination.广东有色金属学报,15.0(002),581. |
| MLA | 胡鹏,et al."Hydrothermal synthesis of boehmites with various particle sizes and transition to α-Al2O3 powders by calcination".广东有色金属学报 15.0.002(2005):581. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。