Effects of irradiation temperature on Ne ion irradiated binary nickel-based alloys
文献类型：期刊论文
| 作者 | Cao, MP; Chen, HC; Zhang, W; Ming, T; Wang, YQ; Yan, L |
| 刊名 | PHILOSOPHICAL MAGAZINE
 |
| 出版日期 | 2020 |
| 卷号 | 100期号:24页码:3061-3069 |
| 关键词 | MICROSTRUCTURAL EVOLUTION NI CORROSION BUBBLES DAMAGE TEM |
| ISSN号 | 1478-6435 |
| DOI | 10.1080/14786435.2020.1804636 |
| 文献子类 | 期刊论文 |
| 英文摘要 | The evolution processes of the defects in Ni, Ni-Cr and Ni-Mo alloys under 400 keV Ne ion irradiation at different temperatures were investigated. At room temperature, the defect sizes are between 2 and 4 nm and defect densities are in the range of 1.24 x 10(15)-1.39 x 10(15)m(-2). With increasing irradiation temperature, the defect sizes become larger, and the defect densities decrease. Moreover, under irradiation at high temperature, Ni-Mo and Ni-Cr alloys show the higher defect densities and smaller defect sizes than Ni. These are ascribed to the pinning effects of solid solution elements on the ion irradiation-induced defects in the nickel-based alloys. |
| 语种 | 英语 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/32832]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 作者单位 | 1.Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China 2.Chinese Acad Sci, Inst High Energy Phys, Beijing, Peoples R China 3.Univ Chinese Acad Sci, Beijing, Peoples R China 4.Los Alamos Natl Lab, Los Alamos, NM USA 5.Clemson Univ, Dept Mat Sci & Engn, Clemson, SC USA |
| 推荐引用方式 GB/T 7714 | Cao, MP,Chen, HC,Zhang, W,et al. Effects of irradiation temperature on Ne ion irradiated binary nickel-based alloys[J]. PHILOSOPHICAL MAGAZINE,2020,100(24):3061-3069. |
| APA | Cao, MP,Chen, HC,Zhang, W,Ming, T,Wang, YQ,&Yan, L.(2020).Effects of irradiation temperature on Ne ion irradiated binary nickel-based alloys.PHILOSOPHICAL MAGAZINE,100(24),3061-3069. |
| MLA | Cao, MP,et al."Effects of irradiation temperature on Ne ion irradiated binary nickel-based alloys".PHILOSOPHICAL MAGAZINE 100.24(2020):3061-3069. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。