Electroplating titanium film on 316L stainless steel in LiCl-KCl-Tix+ (2 < x < 3) molten salts
文献类型：期刊论文
| 作者 | Liu, JX; Liu, JC; Long, DW; Zhan, K |
| 刊名 | NUCLEAR SCIENCE AND TECHNIQUES
 |
| 出版日期 | 2020 |
| 卷号 | 31期号:5页码:43 |
| 关键词 | HIGH-PURITY TITANIUM NACL-KCL ELECTROCHEMICAL-BEHAVIOR REFRACTORY-METALS EUTECTIC MELT CARBON-STEEL IONS ELECTRODEPOSITION EQUILIBRIUM ELECTROLYSIS |
| ISSN号 | 2210-3147 |
| 文献子类 | 期刊论文 |
| 英文摘要 | To improve the anti-corrosion properties of 316L stainless steel, titanium (Ti) metal films were electroplated on it using LiCl-KCl molten salts as the electrolyte, and low-valence Tix+ (2 < x<3) as the solute. The solute was produced by the reaction of Ti4+ and Ti-0 via mixing K2TiF6, and Ti metal (sponge Ti) in the melts. Anti-corrosion test has shown significant enhancement in the stability of the Ti-coated 316L due to the presence of Ti film. However, the anti-corrosion properties did not enhance with an increase in the thickness of the Ti layers owing to a possible defect in the thicker Ti layers. |
| 语种 | 英语 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/32844]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 作者单位 | 1.Chinese Acad Sci, Shanghai Inst Appl Phys, Dept Molten Salt Chem & Engn, Shanghai 201800, Peoples R China 2.Univ Shanghai Sci & Technol, Sch Mat Sci & Engn, Shanghai 200093, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 4.Chinese Acad Sci, Key Lab Interfacial Phys & Technol, Shanghai 201800, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, JX,Liu, JC,Long, DW,et al. Electroplating titanium film on 316L stainless steel in LiCl-KCl-Tix+ (2 < x < 3) molten salts[J]. NUCLEAR SCIENCE AND TECHNIQUES,2020,31(5):43. |
| APA | Liu, JX,Liu, JC,Long, DW,&Zhan, K.(2020).Electroplating titanium film on 316L stainless steel in LiCl-KCl-Tix+ (2 < x < 3) molten salts.NUCLEAR SCIENCE AND TECHNIQUES,31(5),43. |
| MLA | Liu, JX,et al."Electroplating titanium film on 316L stainless steel in LiCl-KCl-Tix+ (2 < x < 3) molten salts".NUCLEAR SCIENCE AND TECHNIQUES 31.5(2020):43. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。