Synthesis of silicon oxycarbonitride nanosphere as cathode host for lithium-sulfur batteries
文献类型：期刊论文
| 作者 | Lu, Jiqun1,2,3; Hu, Jinlong2; Zhong, Haoxiang2; Ren, Yilun2; Zhang, Lingzhi2
|
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2021-04-15 |
| 卷号 | 860页码:10 |
| 关键词 | Silicon oxycarbonitride SiOCN Lithium-sulfur battery Physical and chemical adsorption Lithium polysulfide shuttling |
| ISSN号 | 0925-8388 |
| DOI | 10.1016/j.jallcom.2020.157903 |
| 通讯作者 | Zhang, Lingzhi(lzzhang@ms.giec.ac.cn) |
| 英文摘要 | Silicon oxycarbonitride (SiOCN) composites with different carbon contents were synthesized by pyrolysis of precursors generated from aldimine condensation of 3-aminopropyltriethoxysilane (APTES) with different aldehydes and simultaneous hydrolysis of APTES. Both SiOCN-1 and SiOCN-5 composites, derived from formaldehyde and glutaraldehyde respectively, display similar bulky structure composed by aggregated nanospheres with a diameter of 70-100 nm. SiOCN-5 has a higher carbon content of 30.4% than 15.9% for SiOCN-1, while a lower specific surface area of 38.2 m(2) g(-1) than 76.0 m(2) g(-1) for SiOCN-1. SiOCN/S cathodes with sulfur loading of 1.2-1.5 mg cm(-2) were fabricated using SiOCN as sulfur host on different current collector of aluminum foil (AL) or carbon paper (CP). When using aluminum foil as current collector, SiOCN-5/S-AL cathode exhibits better electrochemical performance than SiOCN-1/S-AL, primarily due to the higher electrical conductivity of SiOCN-5 comparing with SiOCN-1. When using porous carbon paper as current collector, SiOCN-5/S-CP cathode shows the best cycling performance with a discharge capacity of 648.9 mA h g(-1) at 0.2C after 100 cycles. Even at a high rate of 1C, SiOCN-5/SCP also exhibits an excellent cycling stability, delivering a reversible discharge capacity of 374.5 mA h g(-1) after 500 cycles with a capacity retention of 73.0%. (C) 2020 Elsevier B.V. All rights reserved. |
| 资助项目 | National Natural Science Foundation of China[21573239] ; K.C. Wong Education Foundation |
| WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000614154600008 |
| 出版者 | ELSEVIER SCIENCE SA |
| 资助机构 | National Natural Science Foundation of China ; K.C. Wong Education Foundation |
| 源URL | [http://ir.giec.ac.cn/handle/344007/32565]  |
| 专题 | 中国科学院广州能源研究所 |
| 通讯作者 | Zhang, Lingzhi |
| 作者单位 | 1.Guangdong Prov Key Lab New & Renewable Energy Res, Guangzhou 510640, Guangdong, Peoples R China 2.Chinese Acad Sci, Guangzhou Inst Energy Convers, Key Lab Renewable Energy, Guangzhou 510640, Guangdong, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Lu, Jiqun,Hu, Jinlong,Zhong, Haoxiang,et al. Synthesis of silicon oxycarbonitride nanosphere as cathode host for lithium-sulfur batteries[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2021,860:10. |
| APA | Lu, Jiqun,Hu, Jinlong,Zhong, Haoxiang,Ren, Yilun,&Zhang, Lingzhi.(2021).Synthesis of silicon oxycarbonitride nanosphere as cathode host for lithium-sulfur batteries.JOURNAL OF ALLOYS AND COMPOUNDS,860,10. |
| MLA | Lu, Jiqun,et al."Synthesis of silicon oxycarbonitride nanosphere as cathode host for lithium-sulfur batteries".JOURNAL OF ALLOYS AND COMPOUNDS 860(2021):10. |
入库方式： OAI收割
来源：广州能源研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。