Composite adsorbents of CaCI2 and sawdust prepared by carbonization for ammonia adsorption refrigeration
文献类型：期刊论文
| 作者 | Wang Lingbao; Lu Zhenneng; Ma Weibin ; Bu Xianbiao; Li Huashan
|
| 刊名 | 能源前沿：英文版
 |
| 出版日期 | 2012 |
| 卷号 | 6.0期号:004页码:356 |
| 关键词 | 复合吸附剂 吸附式制冷 炭化温度 氯化钙 木屑 CaCl2 复合吸收剂 NH3 |
| ISSN号 | 2095-1701 |
| 英文摘要 | Composite adsorbents of CaC12 and sawdust prepared by carbonization for adsorption refrigeration with NH3 as refrigerant are tested, and the effects of carboniza tion temperature on the sorption capacity and rate are analyzed. The results show that the amount of pores in the sawdust of the composite adsorbents carbonized, apart from the content of CaCI2, is the most dominant factor influencing the NH3 sorption on composite adsorbents. The optimum carbonization temperature is 700℃, which gives the maximal NH3 sorption capacity as high as 0.774 kg of NH3 per kg of the composite, and the specific cooling power is approximately between 338 and 869 W/kg with the cycle duration varying from 5 to 20 minutes. The present study demonstrates that the composite absorbent of CaC12 and sawdust prepared by carbonization is more promising and competitive for adsorption refrigeration application. |
| 语种 | 英语 |
| 源URL | [http://ir.giec.ac.cn/handle/344007/33969]  |
| 专题 | 中国科学院广州能源研究所 |
| 作者单位 | 中国科学院广州能源研究所 |
| 推荐引用方式 GB/T 7714 | Wang Lingbao,Lu Zhenneng,Ma Weibin,et al. Composite adsorbents of CaCI2 and sawdust prepared by carbonization for ammonia adsorption refrigeration[J]. 能源前沿：英文版,2012,6.0(004):356. |
| APA | Wang Lingbao,Lu Zhenneng,Ma Weibin,Bu Xianbiao,&Li Huashan.(2012).Composite adsorbents of CaCI2 and sawdust prepared by carbonization for ammonia adsorption refrigeration.能源前沿：英文版,6.0(004),356. |
| MLA | Wang Lingbao,et al."Composite adsorbents of CaCI2 and sawdust prepared by carbonization for ammonia adsorption refrigeration".能源前沿：英文版 6.0.004(2012):356. |