The effect of crystallite size on low-temperature hydrothermal stability of Cu-SAPO-34
文献类型：期刊论文
| 作者 | Du, Jinpeng ; Shi, Xiaoyan; Shan, Yulong; Wang, Yingjie; Zhang, Wenshuo; Yu, Yunbo; Shan, Wenpo; He, Hong
|
| 刊名 | CATALYSIS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2020-05-07 |
| 卷号 | 10期号:9页码:2855-2863 |
| ISSN号 | 2044-4753 |
| 英文摘要 | Two Cu-SAPO-34 samples with similar chemical compositions but different crystallite sizes of 10 mu m and 2 mu m, respectively, were obtained by modifying crystallization conditions. The effect of crystallite size on the low-temperature hydrothermal stability of Cu-SAPO-34 was comparatively investigated. The results showed that Cu-SAPO-34 with smaller particle size possessed better resistance to treatment at 70 degrees C in humid conditions. During low-temperature hydrothermal aging, isolated Cu2+ species in Cu-SAPO-34 tended to be attacked by water vapor to form Cu(OH)(2) species, which can combine with extra-framework Al to form inactive CuAl2O4 species. The superior stability of Cu-SAPO-34 with smaller crystallite size is primarily attributed to the lower Cu concentration on the crystal surface compared with the sample with larger particle size. Thus, more active Cu sites were maintained on small-size Cu-SAPO-34 after low-temperature hydrothermal aging. |
| 源URL | [http://ir.rcees.ac.cn/handle/311016/44557]  |
| 专题 | 生态环境研究中心_大气污染控制中心 |
| 推荐引用方式 GB/T 7714 | Du, Jinpeng,Shi, Xiaoyan,Shan, Yulong,et al. The effect of crystallite size on low-temperature hydrothermal stability of Cu-SAPO-34[J]. CATALYSIS SCIENCE & TECHNOLOGY,2020,10(9):2855-2863. |
| APA | Du, Jinpeng.,Shi, Xiaoyan.,Shan, Yulong.,Wang, Yingjie.,Zhang, Wenshuo.,...&He, Hong.(2020).The effect of crystallite size on low-temperature hydrothermal stability of Cu-SAPO-34.CATALYSIS SCIENCE & TECHNOLOGY,10(9),2855-2863. |
| MLA | Du, Jinpeng,et al."The effect of crystallite size on low-temperature hydrothermal stability of Cu-SAPO-34".CATALYSIS SCIENCE & TECHNOLOGY 10.9(2020):2855-2863. |
入库方式： OAI收割
来源：生态环境研究中心
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。