Transfer from M3B2 boride to BN nitride in 9Cr3W3CoB martensitic heat-resistant steel
文献类型：期刊论文
| 作者 | Liang, Ye1,2; Yan, Wei1,3; Shi, Xianbo1,3; Li, Yanfen1,3; Wang, Wei1,3; Shi, Quanqiang1,3; Shan, Yiyin1,3; Yang, Ke1,3 |
| 刊名 | JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T
 |
| 出版日期 | 2021-07-01 |
| 卷号 | 13页码:513-523 |
| 关键词 | M3B2 BN Aging Precipitation Morphology |
| ISSN号 | 2238-7854 |
| DOI | 10.1016/j.jmrt.2021.05.004 |
| 通讯作者 | Yan, Wei(weiyan@imr.ac.cn) ; Yang, Ke(kyang@imr.ac.cn) |
| 英文摘要 | Boron is generally added into heat-resistant steel to improve the creep strength. The existence of M3B2 borides and BN nitrides should be avoided due to the consumption of effective B. Before eliminating the harmful borides, it is important to elucidate their thermodynamic behavior during aging. Therefore, the formation of BN nitride in a 9Cr3W3CoB steel during high temperature aging was investigated. It was found that majority of B was presented as M3B2 borides in the as-treated steel. Due to the low content of N and the existence of M3B2 borides, only a few BN nitrides were distributed along PAGBs. Metastable M3B2 borides would gradually dissolve during isothermal exposure and then lead to the precipitation of BN nitride, which has been verified by employing thermo-mechanical treatment (TMT) to eliminate M3B2 borides. It was revealed under scanning electron microscopy (SEM) that BN could not precipitate during high temperature aging in the TMT sample without M3B2 borides. The nucleation and growth of BN nitride was thermodynamic processes affected by both aging time and temperature. Its number density and size increased with increasing aging temperature. During aging at 800 degrees C, BN nitride nucleated quickly and the shape evolved from subsphaeroidal to irregular even with sharp corners. Unfortunately, the BN particles with sharp corners were detrimental to toughness. (C) 2021 The Authors. Published by Elsevier B.V. |
| 资助项目 | National Natural Science Foundation of China[51971226] ; National Basic Research Program of China[2017YFB 0305201] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000677670200009 |
| 出版者 | ELSEVIER |
| 资助机构 | National Natural Science Foundation of China ; National Basic Research Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/159638]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yan, Wei; Yang, Ke |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liang, Ye,Yan, Wei,Shi, Xianbo,et al. Transfer from M3B2 boride to BN nitride in 9Cr3W3CoB martensitic heat-resistant steel[J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T,2021,13:513-523. |
| APA | Liang, Ye.,Yan, Wei.,Shi, Xianbo.,Li, Yanfen.,Wang, Wei.,...&Yang, Ke.(2021).Transfer from M3B2 boride to BN nitride in 9Cr3W3CoB martensitic heat-resistant steel.JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T,13,513-523. |
| MLA | Liang, Ye,et al."Transfer from M3B2 boride to BN nitride in 9Cr3W3CoB martensitic heat-resistant steel".JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T 13(2021):513-523. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。