Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging
文献类型：期刊论文
| 作者 | Xiao, Xiaopeng1,2; Li, Dianzhong2; Li, Yiyi2,3; Lu, Shanping2 |
| 刊名 | MATERIALS CHARACTERIZATION
 |
| 出版日期 | 2021-08-01 |
| 卷号 | 178页码:11 |
| 关键词 | Stress relaxation cracking Austenitic stainless steel weld metal Grain boundary misorientation Depletion of Cr |
| ISSN号 | 1044-5803 |
| DOI | 10.1016/j.matchar.2021.111309 |
| 通讯作者 | Lu, Shanping(shplu@imr.ac.cn) |
| 英文摘要 | Stress relaxation cracking failure is widely reported in the materials used for thermal power plants, which seriously affected the safety of thermal power units under long-term service. In our study, the influence of intergranular precipitation behavior on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal was investigated based on the pre-compressed CT technique. The 45 degrees misorientation grain boundary has the lowest critical interfacial nucleation energy, followed by the grain boundaries away from the 45 degrees misorientation. As a result, the coarse intergranular M23C6 carbides were more prone to precipitate at 45 degrees misorientation grain boundary, which led to the lowest resistance to stress relaxation cracking susceptibility at 35 to 45 degrees grain boundary. Further analysis indicated that intergranular cavities were easily initiated at the noncoherent M23C6/gamma interface. Since the non-coherent interface with a low Cr concentration zone and high specific interfacial energy had a lower strength, the lattice distortion at the non-coherent interface could lead to higher strain concentration. |
| 资助项目 | Shenyang National Laboratory for Materials Science Innovation[L2019R35] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000678042300002 |
| 出版者 | ELSEVIER SCIENCE INC |
| 资助机构 | Shenyang National Laboratory for Materials Science Innovation |
| 源URL | [http://ir.imr.ac.cn/handle/321006/159735]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Lu, Shanping |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xiao, Xiaopeng,Li, Dianzhong,Li, Yiyi,et al. Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging[J]. MATERIALS CHARACTERIZATION,2021,178:11. |
| APA | Xiao, Xiaopeng,Li, Dianzhong,Li, Yiyi,&Lu, Shanping.(2021).Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging.MATERIALS CHARACTERIZATION,178,11. |
| MLA | Xiao, Xiaopeng,et al."Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging".MATERIALS CHARACTERIZATION 178(2021):11. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。