Comparison of the corrosion behavior of AM60 Mg alloy with and without self-healing coating in atmospheric environment
文献类型：期刊论文
| 作者 | Song, Yingwei1; Liu, Dan1,2; Tang, Weineng3; Dong, Kaihui1; Shan, Dayong1; Han, En-Hou1 |
| 刊名 | JOURNAL OF MAGNESIUM AND ALLOYS
 |
| 出版日期 | 2021-07-15 |
| 卷号 | 9期号:4页码:1220-1232 |
| 关键词 | Self-healing coating Micro-arc oxidation (mao) film Atmospheric corrosion Mg alloy Inhibitor Sediments |
| ISSN号 | 2213-9567 |
| DOI | 10.1016/j.jma.2020.05.018 |
| 通讯作者 | Song, Yingwei(ywsong@imr.ac.cn) |
| 英文摘要 | Coatings on the surface of Mg alloys are inevitably damaged during their practical applications, and corrosion can easily initiate from the damaged areas to accelerate the failure of Mg parts. A dual self-healing coating has already been developed to solve this problem in our previous work. Considering the practical application of this coating, it is necessary to investigate its service behavior in atmospheric environment. Thus, the corrosion behavior of AM60 Mg substrate with and without the self-healing coating was compared in Shenyang industrial atmospheric environment. The results show that the enrichment of sediments and rainwater on the scratch areas can accelerate the corrosion of the exposed Mg substrate. The inhibitors can be released from the damaged coating to inhibit corrosion. The dual self-healing coating shows better inhibition ability to narrow scratches due to the higher inhibitor concentration and less resumption. Also, the coating with wide scratches displays enough inhibition ability as well. The dual self-healing coating is a good alternative for Mg alloy parts in the practical applications. (C) 2020 Chongqing University. Publishing service provided by Elsevier B.V. on behalf of KeAi Communications Co. Ltd. |
| 资助项目 | National Natural Science Foundation of China[51671199] ; National Key Research and Development Program of China[2016 YFB0301105] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000669899200008 |
| 出版者 | KEAI PUBLISHING LTD |
| 资助机构 | National Natural Science Foundation of China ; National Key Research and Development Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/159962]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Song, Yingwei |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 3.China Baowu Grp, Baosteel Cent Res Inst, R&D Ctr, 655 Fujin Rd, Shanghai 201900, Peoples R China |
| 推荐引用方式 GB/T 7714 | Song, Yingwei,Liu, Dan,Tang, Weineng,et al. Comparison of the corrosion behavior of AM60 Mg alloy with and without self-healing coating in atmospheric environment[J]. JOURNAL OF MAGNESIUM AND ALLOYS,2021,9(4):1220-1232. |
| APA | Song, Yingwei,Liu, Dan,Tang, Weineng,Dong, Kaihui,Shan, Dayong,&Han, En-Hou.(2021).Comparison of the corrosion behavior of AM60 Mg alloy with and without self-healing coating in atmospheric environment.JOURNAL OF MAGNESIUM AND ALLOYS,9(4),1220-1232. |
| MLA | Song, Yingwei,et al."Comparison of the corrosion behavior of AM60 Mg alloy with and without self-healing coating in atmospheric environment".JOURNAL OF MAGNESIUM AND ALLOYS 9.4(2021):1220-1232. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。