Quantifying the Influences of Carbides and Porosities on the Fatigue Crack Evolution of a Ni-Based Single-Crystal Superalloy using X-ray Tomography
文献类型：期刊论文
| 作者 | Liu, Keli1; Wang, Junsheng1,2; Wang, Bing1; Mao, Pengcheng3; Yang, Yanhong4; Zhou, Yizhou4 |
| 刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| 出版日期 | 2021-07-16 |
| 页码 | 13 |
| 关键词 | X-ray tomography Ni-based superalloys Fatigue Porosity Carbide Crack initiation Crack propagation |
| ISSN号 | 1006-7191 |
| DOI | 10.1007/s40195-021-01273-7 |
| 通讯作者 | Wang, Junsheng(junsheng.wang@bit.edu.cn) |
| 英文摘要 | The detrimental effects of carbides and porosity on the fatigue crack initiation and propagation of nickel-based single-crystal superalloys have been reported by many previous studies. However, few studies have quantitatively compared the fatigue damaging effects of carbides and pores on the fatigue crack evolution. In this study, a high-resolution X-ray computed tomography (XCT) characterization of a DD5 nickel-based single-crystal superalloy during fatigue test was performed. The evolution of carbides, pores and cracks at all stages was observed and tracked. In order to quantify the 3D microstructures, a new damage factor that correlates the morphology of fracture surface with crack evolution behaviors was proposed. It was found that porosity was more detrimental than carbides in crack initiation and propagation during fatigue tests. Furthermore, pore spacing has been found to be the most significant factor among all controlling pore characteristics in the crack initiation stage and sphericity is the most critical pore characteristic in the crack propagation stage. Therefore, by statistically analyzing the evolution of carbides and pores during fatigue tests in this study, the underlying fatigue cracking mechanism of nickel-based superalloys is revealed. |
| 资助项目 | Ministry of Industry and Information Technology through the National Science and Technology Major Project of China[2017-VI-0003-0073] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000673256600002 |
| 出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
| 资助机构 | Ministry of Industry and Information Technology through the National Science and Technology Major Project of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/160191]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, Junsheng |
| 作者单位 | 1.Beijing Inst Technol, Sch Mat Sci & Engn, Beijing 100081, Peoples R China 2.Beijing Inst Technol, Adv Res Inst Multidisciplinary Sci, Beijing 100081, Peoples R China 3.Beijing Inst Technol, Ctr Micro & Nano Technol, Beijing 100081, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Superalloys Div, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Keli,Wang, Junsheng,Wang, Bing,et al. Quantifying the Influences of Carbides and Porosities on the Fatigue Crack Evolution of a Ni-Based Single-Crystal Superalloy using X-ray Tomography[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2021:13. |
| APA | Liu, Keli,Wang, Junsheng,Wang, Bing,Mao, Pengcheng,Yang, Yanhong,&Zhou, Yizhou.(2021).Quantifying the Influences of Carbides and Porosities on the Fatigue Crack Evolution of a Ni-Based Single-Crystal Superalloy using X-ray Tomography.ACTA METALLURGICA SINICA-ENGLISH LETTERS,13. |
| MLA | Liu, Keli,et al."Quantifying the Influences of Carbides and Porosities on the Fatigue Crack Evolution of a Ni-Based Single-Crystal Superalloy using X-ray Tomography".ACTA METALLURGICA SINICA-ENGLISH LETTERS (2021):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。