Microstructural evolution of a Y2O3 network reinforced Ni-Co based superalloy fabricated by spark plasma sintering
文献类型：期刊论文
| 作者 | Bai, Yingbo1,2; Zhang, Rui2; Qi, Yang1; Cui, Chuanyong2; Cai, Yahui1 |
| 刊名 | VACUUM
 |
| 出版日期 | 2021-04-01 |
| 卷号 | 186页码:12 |
| ISSN号 | 0042-207X |
| 关键词 | Reinforcement network distribution Spark plasma sintering Ni-Co based Superalloy Microstructural evolution |
| DOI | 10.1016/j.vacuum.2020.110033 |
| 通讯作者 | Zhang, Rui(rzhang@imr.ac.cn) |
| 英文摘要 | A Y2O3 network reinforced Ni-Co based superalloy was prepared by ball milling and spark plasma sintering (SPS). Ball milling time and solution treatment temperature were studied to obtain the best microstructure. Optical microscope (OM), scanning electron microscope (SEM) and electron probe micro-analyzer (EPMA) were used to observe the microstructure evolution of as-sintered and solution-treated samples. Hardness also was conducted to analysis the variations of properties with the increase of solution-treatment temperature. The results revealed that the ball milling was beneficial to sintering activity of Ni-Co based superalloy powders. The Y-containing oxides in as-sintered alloys exhibited a network distribution. Master alloy with low C content made the microstructure more uniform during the sintering. After solution treatment at 1250 degrees C, the precipitations in the Y2O3 network reinforced Ni-Co based superalloy with low C content were fine nano tertiary.' phase with the size of similar to 30 nm. In the Vickers hardness test, Y-containing oxides provided additional hardness for the alloy. The appropriate solution treatment temperature and master alloy with low C content were beneficial to obtain better microstructure and properties of the alloy. |
| 资助项目 | National Key R&D Program of China[2019YFA0705304] ; National Key R&D Program of China[2017YFA0700703] ; Doctoral Start-up Foundation of Liaoning Province ; National Natural Science Foundation of China[51671189] |
| WOS研究方向 | Materials Science ; Physics |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| WOS记录号 | WOS:000656846700005 |
| 资助机构 | National Key R&D Program of China ; Doctoral Start-up Foundation of Liaoning Province ; National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/160278]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, Rui |
| 作者单位 | 1.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Bai, Yingbo,Zhang, Rui,Qi, Yang,et al. Microstructural evolution of a Y2O3 network reinforced Ni-Co based superalloy fabricated by spark plasma sintering[J]. VACUUM,2021,186:12. |
| APA | Bai, Yingbo,Zhang, Rui,Qi, Yang,Cui, Chuanyong,&Cai, Yahui.(2021).Microstructural evolution of a Y2O3 network reinforced Ni-Co based superalloy fabricated by spark plasma sintering.VACUUM,186,12. |
| MLA | Bai, Yingbo,et al."Microstructural evolution of a Y2O3 network reinforced Ni-Co based superalloy fabricated by spark plasma sintering".VACUUM 186(2021):12. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。