Dealloying corrosion of anodic and nanometric Mg41Nd5 in solid solution-treated Mg-3Nd-1Li-0.2Zn alloy
文献类型：期刊论文
| 作者 | Gao, Gui-Jia2; Zeng, Mei-Qi2; Zhang, En-Liang2; Zeng, Rong-Chang2,3; Cui, Lan-Yue2; Xu, Dao-kui1; Wang, Feng-Qin2; Kannan, M. Bobby4 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2021-08-30 |
| 卷号 | 83页码:161-178 |
| 关键词 | Magnesium alloy Corrosion Second phase Rare metal Dealloying |
| ISSN号 | 1005-0302 |
| DOI | 10.1016/j.jmst.2020.12.049 |
| 通讯作者 | Zeng, Rong-Chang(rczeng@foxmail.com) ; Wang, Feng-Qin(skdwangfengqin@163.com) |
| 英文摘要 | The microstructure and chemical compositions of the solid solution-treated Mg-3Nd-1Li-0.2Zn alloy were characterized using optical microscope, scanning electron microscope (SEM), transmission electron microscope (TEM), electron probe micro-analyzer (EPMA) and X-ray photoelectron spectroscopy (XPS). The corrosion behaviour of the alloy was investigated via electrochemical polarization, electrochemical impedance spectroscopy (EIS), hydrogen evolution test and scanning Kelvin probe (SKP). The results showed that the microstructure of the as-extruded Mg-3Nd-1Li-0.2Zn alloy contained alpha-Mg matrix and nanometric second phase Mg41Nd5. The grain size of the alloy increased significantly with the increase in the heat-treatment duration, whereas the volume fraction of the second phase decreased after the solid solution treatment. The surface film was composed of oxides (Nd2O3, MgO, Li2O and ZnO) and carbonates (MgCO3 and Li2CO3), in addition to Nd. The as-extruded alloy exhibited the best corrosion resistance after an initial soaking of 10 min, whereas the alloy with 4h-solution-treatment possessed the lowest corrosion rate after a longer immersion (1 h). This can be attributed to the formation of Nd-containing oxide film on the alloys and a dense corrosion product layer. The dealloying corrosion of the second phase was related to the anodic Mg41Nd5 with a more negative Volta potential relative to alpha-Mg phase. The preferential corrosion of Mg41Nd5 is proven by in-situ observation and SEM. The solid solution treatment of Mg-3Nd-1Li-0.2Zn alloy led to a shift in corrosion type from pitting corrosion to uniform corrosion under long-term exposure. (C) 2021 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 资助项目 | National Natural Science Foundation of China[52071191] ; SDUST Research Found[2014TDJH104] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000661886200016 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| 资助机构 | National Natural Science Foundation of China ; SDUST Research Found |
| 源URL | [http://ir.imr.ac.cn/handle/321006/160481]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zeng, Rong-Chang; Wang, Feng-Qin |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 2.Shandong Univ Sci & Technol, Coll Mat Sci & Engn, Corros Lab Light Met, Qingdao 266590, Peoples R China 3.Zhengzhou Univ, Sch Mat Sci & Engn, Zhengzhou 450002, Peoples R China 4.Univ Newcastle, Sch Engn, Callaghan, NSW 2308, Australia |
| 推荐引用方式 GB/T 7714 | Gao, Gui-Jia,Zeng, Mei-Qi,Zhang, En-Liang,et al. Dealloying corrosion of anodic and nanometric Mg41Nd5 in solid solution-treated Mg-3Nd-1Li-0.2Zn alloy[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2021,83:161-178. |
| APA | Gao, Gui-Jia.,Zeng, Mei-Qi.,Zhang, En-Liang.,Zeng, Rong-Chang.,Cui, Lan-Yue.,...&Kannan, M. Bobby.(2021).Dealloying corrosion of anodic and nanometric Mg41Nd5 in solid solution-treated Mg-3Nd-1Li-0.2Zn alloy.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,83,161-178. |
| MLA | Gao, Gui-Jia,et al."Dealloying corrosion of anodic and nanometric Mg41Nd5 in solid solution-treated Mg-3Nd-1Li-0.2Zn alloy".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 83(2021):161-178. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。