Effects of solution treatment on microstructure and tensile properties of as-cast alloy 625
文献类型：期刊论文
| 作者 | Yang, Fei1,2; Hou, Jie-shan1; Wang, Chang-shuai1; Zhou, Lan-zhang1 |
| 刊名 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
 |
| 出版日期 | 2021-02-01 |
| 卷号 | 31期号:1页码:426-437 |
| 关键词 | as-cast alloy 625 solution treatment microstructure tensile properties gamma/Laves eutectic |
| ISSN号 | 1003-6326 |
| DOI | 10.1016/S1003-6326(21)65507-3 |
| 通讯作者 | Hou, Jie-shan(jshou@imr.ac.cn) ; Zhou, Lan-zhang(lzz@imr.ac.cn) |
| 英文摘要 | Effects of solution treatment between 1050 and 1250 degrees C on microstructure and tensile properties of as-cast alloy 625 were investigated. The microstructure and solidification characteristics of the alloy were studied by SEM, EDS, EPMA and DTA. The results showed that the solidification sequence of the alloy should be written as L -> L+gamma -> L+gamma+MC -> L+gamma+MC+gamma/Laves ->gamma+MC+gamma/Laves. After solution treatment at 1225 and 1250 degrees C, incipient melting of Laves phase was observed. The ultimate tensile strength decreased monotonically with the increase of solution treatment temperature, and the yield strength had no significant variation. The elongation increased slightly at first and then reached a minimum value at 1250 degrees C. The fracture mechanism changed from transgranular mode to intergranular mode after solution at 1250 degrees C for the reason that numerous Laves phases melted at grain boundaries and microcracks nucleated in the molten pool. The suitable solution treatment temperature of this alloy was 1200 degrees C. |
| 资助项目 | National Natural Science Foundation of China[51571191] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000617542200010 |
| 出版者 | ELSEVIER |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/160792]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Hou, Jie-shan; Zhou, Lan-zhang |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang, Fei,Hou, Jie-shan,Wang, Chang-shuai,et al. Effects of solution treatment on microstructure and tensile properties of as-cast alloy 625[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2021,31(1):426-437. |
| APA | Yang, Fei,Hou, Jie-shan,Wang, Chang-shuai,&Zhou, Lan-zhang.(2021).Effects of solution treatment on microstructure and tensile properties of as-cast alloy 625.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,31(1),426-437. |
| MLA | Yang, Fei,et al."Effects of solution treatment on microstructure and tensile properties of as-cast alloy 625".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 31.1(2021):426-437. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。