A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern

文献类型：期刊论文

作者Li, Cong2,3; Fang, Xiaodong2,4; Wang, Qingsheng2; Shen, Mingli5; Wang, Haoliang6; Zeng, Xian7; Liu, Yujing1; Meng, Gang2
刊名CORROSION SCIENCE
出版日期2021-03-01
卷号180页码:17
ISSN号0010-938X
关键词T91 Oxygen-saturated LBE Oxidation Erosion Impact angle Cottrell atmosphere
DOI10.1016/j.corsci.2020.109214
通讯作者Fang, Xiaodong(xdfang@aiofm.ac.cn) ; Wang, Qingsheng(qswang@aiofm.ac.cn) ; Shen, Mingli(mlshen@imr.ac.cn)
英文摘要This paper reports an attempt to speculate about corrosion resistance of T91 steel to extreme lead-bismuth eutectic (LBE) flow pattern. We build a modified dynamic corrosion apparatus permitting assemblages of oxidation, erosion or dissolution attack proceeding together within oxygen-saturated LBE. After corrosion test at 400 degrees C up to 1000 h, discrepancies of corrosion performance under various flow patterns were described by diffusion or mass transfer kinetics as well as erosion mechanics. In justification of dense Fe-O layer and cracks across oxide scales detected within typical erosion cavities, we put forward oxide growth stress enhanced by high surface curvature.
资助项目Natural Science Foundation of Top Talent of SZTU[2020101] ; CAS (Chinese Academy of Sciences) Pioneer Hundred Talents Program ; National Natural Science Foundation of China[11674324] ; National Natural Science Foundation of China[51803200] ; CAS-JSPS Joint Research Projects[GJHZ1891]
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
语种英语
出版者PERGAMON-ELSEVIER SCIENCE LTD
WOS记录号WOS:000612032300002
资助机构Natural Science Foundation of Top Talent of SZTU ; CAS (Chinese Academy of Sciences) Pioneer Hundred Talents Program ; National Natural Science Foundation of China ; CAS-JSPS Joint Research Projects
源URL[http://ir.imr.ac.cn/handle/321006/160978]  
专题金属研究所_中国科学院金属研究所
通讯作者Fang, Xiaodong; Wang, Qingsheng; Shen, Mingli
作者单位1.Changsha Univ Sci & Technol, Coll Mat Sci & Engn, 960 2nd Sect,Wanjiali RD S, Changsha 410004, Hunan, Peoples R China
2.Chinese Acad Sci, Anhui Inst Opt & Fine Mech, Hefei 230031, Peoples R China
3.Univ Sci & Technol China, Hefei 230026, Peoples R China
4.Shenzhen Technol Univ, Coll New Mat & New Energies, Shenzhen 518118, Guangdong, Peoples R China
5.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Wencui Rd 62, Shenyang 110016, Peoples R China
6.Dongguan Univ Technol, Sch Mech Engn, Dongguan 523808, Peoples R China
7.China Nucl Power Technol Res Inst, Sci & Technol Bldg,1001 Shangbuzhong Rd, Shenzhen 518031, Peoples R China
推荐引用方式
GB/T 7714		 Li, Cong,Fang, Xiaodong,Wang, Qingsheng,et al. A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern[J]. CORROSION SCIENCE,2021,180:17.
APA Li, Cong.,Fang, Xiaodong.,Wang, Qingsheng.,Shen, Mingli.,Wang, Haoliang.,...&Meng, Gang.(2021).A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern.CORROSION SCIENCE,180,17.
MLA Li, Cong,et al."A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern".CORROSION SCIENCE 180(2021):17.

入库方式： OAI收割

来源：金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。