Effects of microstructure evolution on the deformation mechanisms and tensile properties of a new Ni-base superalloy during aging at 800 degrees C
文献类型：期刊论文
| 作者 | Hou, Kunlei1,2; Wang, Min1; Ou, Meiqiong1; Li, Haoze1; Hao, Xianchao1; Ma, Yingche1; Liu, Kui1 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2021-03-30 |
| 卷号 | 68页码:40-52 |
| ISSN号 | 1005-0302 |
| 关键词 | Ni-base superalloy Aging gamma ' size Yield strength Deformation mechanism Fracture behavior |
| DOI | 10.1016/j.jmst.2020.08.001 |
| 通讯作者 | Ou, Meiqiong(mqou@imr.ac.cn) ; Ma, Yingche(ycma@imr.ac.cn) |
| 英文摘要 | Tensile properties at room temperature of a new casting Ni-base superalloy during aging at 800 degrees C for 0-1000 h were investigated. During aging, granular M23C6 carbides presented at grain boundaries and kept growing from dispersed particles to continuous networks. The gamma' phase significantly coarsened, with the morphology of some gamma' phase changed from spherical to rounded cubic shape after 1000 h. Three deformation mechanisms in relation to the gamma' diameter (d(gamma')) were identified: (i) weakly coupled dislocations (WCD) connected by anti-phase boundary (APB) traveled in pair across the gamma/gamma' structure when d(gamma') was small in the under-aged alloys; (ii) strongly coupled dislocations (SCD) with reduced spacing compared to (i) sheared gamma' phase when d(gamma') increased in the over-aged alloys; (iii) dislocations occasionally by-passed gamma' phase when d gamma' was larger than 97 nm after aging for more than 300 h. The alloy obtained the peak strength when 20 h-aged with d(gamma') = 44 nm which was in the transition between (i) and (ii). The aginginduced variation in yield strength was correlated to the coarsening of gamma' phase using a tsyheoretical model of precipitation strengthening in terms of the formation of APB. The calculated results suggested that the gamma' phase with a volume fraction of 23% contributed more than 61% of the peak-aged yield strength. Observation after fracture revealed that the alloys usually fractured at grain boundaries. High stress concentration around carbides resulted in cracks by carbides self-cracking and the initiation of cavities. The undesirable agglomeration of M23C6 at grain boundaries was harmful to the properties of the overaged alloys. (C) 2021 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| WOS记录号 | WOS:000623854600006 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/161339]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ou, Meiqiong; Ma, Yingche |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China |
| 推荐引用方式 GB/T 7714 | Hou, Kunlei,Wang, Min,Ou, Meiqiong,et al. Effects of microstructure evolution on the deformation mechanisms and tensile properties of a new Ni-base superalloy during aging at 800 degrees C[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2021,68:40-52. |
| APA | Hou, Kunlei.,Wang, Min.,Ou, Meiqiong.,Li, Haoze.,Hao, Xianchao.,...&Liu, Kui.(2021).Effects of microstructure evolution on the deformation mechanisms and tensile properties of a new Ni-base superalloy during aging at 800 degrees C.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,68,40-52. |
| MLA | Hou, Kunlei,et al."Effects of microstructure evolution on the deformation mechanisms and tensile properties of a new Ni-base superalloy during aging at 800 degrees C".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 68(2021):40-52. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。