Thickness-dependent oxidation behaviors of Ti3AlC2 foils at 1100?C in air
文献类型:期刊论文
作者 | Li, Xichao2,3; Zheng, Lili1; Qian, Yuhai3; Xu, Jingjun3; Li, Meishuan3 |
刊名 | CORROSION SCIENCE |
出版日期 | 2021-06-01 |
卷号 | 185页码:10 |
ISSN号 | 0010-938X |
关键词 | Ceramic Oxidation Selective oxidation |
DOI | 10.1016/j.corsci.2021.109431 |
通讯作者 | Zheng, Lili(llzhengqdu@163.com) ; Qian, Yuhai(yhqian@imr.ac.cn) |
英文摘要 | The oxidation behavior of Ti3AlC2 foils at 1100 ?C in air has been investigated. It is found that the oxidation behavior of Ti3AlC2 is thickness-dependent. For the 85 ?m thick sample, breakaway oxidation occurs initially. For the 95 ?m thick sample, selective oxidation occurs initially and transforms to breakaway oxidation after 12.5 h. When the thickness exceeds 110 ?m, Ti3AlC2 foils exhibit much longer lifetime. Continuous Al2O3 scale is formed on the 75-120 ?m thick wedge-shaped sample, suggesting that diffusion rate of Al is high in the whole body during oxidation. The mechanism of breakaway oxidation of Ti3AlC2 is discussed. |
资助项目 | National Natural Science Foundation of China[51571205] ; National Natural Science Foundation of China[52001179] ; Natural Science Foundation of Shandong Province[ZR2020ME019] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000643864000001 |
资助机构 | National Natural Science Foundation of China ; Natural Science Foundation of Shandong Province |
源URL | [http://ir.imr.ac.cn/handle/321006/161549] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zheng, Lili; Qian, Yuhai |
作者单位 | 1.Qingdao Univ, Natl Engn Res Ctr Intelligent Elect Vehicle Power, Coll Mech & Elect Engn, Qingdao 266071, Peoples R China 2.CRRC Qingdao Sifang Rolling Stock Res Inst Co Ltd, Energy Saving Business Div, Qingdao 266031, Peoples R China 3.Chinese Acad Sci, Inst Met Res, High Performance Ceram Div, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Xichao,Zheng, Lili,Qian, Yuhai,et al. Thickness-dependent oxidation behaviors of Ti3AlC2 foils at 1100?C in air[J]. CORROSION SCIENCE,2021,185:10. |
APA | Li, Xichao,Zheng, Lili,Qian, Yuhai,Xu, Jingjun,&Li, Meishuan.(2021).Thickness-dependent oxidation behaviors of Ti3AlC2 foils at 1100?C in air.CORROSION SCIENCE,185,10. |
MLA | Li, Xichao,et al."Thickness-dependent oxidation behaviors of Ti3AlC2 foils at 1100?C in air".CORROSION SCIENCE 185(2021):10. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。