Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy
文献类型:期刊论文
作者 | Wang, Qirui1,2; Lei, Xiaofei2; Hu, Ming2; Xu, Xin3; Yang, Rui2; Dong, Limin2 |
刊名 | METALS |
出版日期 | 2021-04-01 |
卷号 | 11期号:4页码:12 |
关键词 | Ti-6Al-6V-2Sn titanium alloy heat treatment microstructure |
DOI | 10.3390/met11040556 |
通讯作者 | Xu, Xin(xuxin58@mail.sysu.edu.cn) ; Dong, Limin(lmdong@imr.ac.cn) |
英文摘要 | The microstructure and tensile properties of Ti-6Al-6V-2Sn alloy heat-treated at different solution and aging temperatures has been systematically investigated. Specimens were solution-treated at 970 degrees C (above the beta transus) and 920 degrees C (below the beta transus), respectively, followed by water quenching. When the alloy is quenched from 970 degrees C, alpha' (hcp) and alpha '' (orthorhombic) martensite phases co-exist in the microstructure. When it is quenched from 920 degrees C, alpha ' martensite phase does not form, while equiaxial primary alpha (alpha(p)) phase and alpha '' are found in the microstructure. The results also show that the strength of the alloy increases but the ductility deteriorates as the solution temperature becomes higher when the aging treatment is unchanged. This is because the volume fraction of equiaxial alpha(p) phase is lower but the volume fraction of the acicular secondary alpha (alpha(s)) phase is higher for higher solution temperature. When the alloy is aged at different temperatures after the solution treatment at 900 degrees C, the strength of the alloy decreases with the increase of aging temperature and the ductility shows the opposite trend as the size of the acicular alpha(s) becomes longer and its volume fraction is lower at higher aging temperature. |
资助项目 | National Science Foundation for Young Scientists of China[51801199] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000643274300001 |
资助机构 | National Science Foundation for Young Scientists of China |
源URL | [http://ir.imr.ac.cn/handle/321006/162059] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Xu, Xin; Dong, Limin |
作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 3.Sun Yat Sen Univ, Sch Mat, Shenzhen 518107, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Qirui,Lei, Xiaofei,Hu, Ming,et al. Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy[J]. METALS,2021,11(4):12. |
APA | Wang, Qirui,Lei, Xiaofei,Hu, Ming,Xu, Xin,Yang, Rui,&Dong, Limin.(2021).Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy.METALS,11(4),12. |
MLA | Wang, Qirui,et al."Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy".METALS 11.4(2021):12. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。