Effect of groove surface texture on the fretting wear of Ti-6Al-4V alloy

文献类型：期刊论文

作者Wang, Jianfei1,2; Xue, Weihai1,2; Gao, Siyang1,2; Li, Shu1,2; Duan, Deli1,2
刊名WEAR
出版日期2021-12-15
卷号486页码:11
关键词Titanium alloy Fretting wear Laser surface texture Groove texture Debris
ISSN号0043-1648
DOI10.1016/j.wear.2021.204079
通讯作者Xue, Weihai(whxue@imr.ac.cn) ; Duan, Deli(duandl@imr.ac.cn)
英文摘要Groove surface textures with different orientations and spacings were prepared on the Ti-6Al-4V alloy by using a laser. Fretting tests (rubbed with a Ti-6Al-4V ball) were conducted under different textures, and the coefficient of friction (COF) curves, system deformation and wear morphologies were analysed in detail. The groove orientations to the fretting direction affected the fretting wear behaviour through the following ways: (1) Fretting tests on different groove orientations resulted in different fretting loop shapes at the initial stage of fretting wear. (2) The COF curves of fretting test on perpendicular grooves and 45 degrees grooves were similar. COF presented a sharp increase after approximately 1000 cycles under relatively low loads. The COF curves of fretting test on parallel grooves and untextured surface were similar. Only a small oscillation of COF was observed during the whole fretting tests. (3) When fretting was run in gross slip regime, the magnitude of system deformation was perpendicular grooves, no-texture samples, 45 degrees grooves, and parallel grooves in order. The above results may have resulted from the influence of surface textures on the formation and development of wear debris. For the perpendicular grooves, high pressure was recorded in partial slip regime cracks, and peeling appeared on the convex platform of samples with the groove spacing of 80 um, and this phenomenon promoted the formation of debris. Moreover, the perpendicular grooves prevented debris from spilling out of contact areas. For the parallel grooves, the filling mechanism of grooves was found, in which the material in the upper layer gradually squeezed the material in the lower layer toward the centre and bottom of the groove, and the parallel grooves accelerated debris from spilling out of contact areas. Therefore, groove surface textures may adjust the fretting regime of titanium alloys by changing the orientation and spacing, which could provide a new tribology design for fretting friction pairs.
资助项目Liaoning Key Laboratory of Aero-engine Material Tribology ; Strategic Priority Research Program of the Chinese Academy of Sciences[XDC04040400]
WOS研究方向Engineering ; Materials Science
语种英语
WOS记录号WOS:000697122700001
出版者ELSEVIER SCIENCE SA
资助机构Liaoning Key Laboratory of Aero-engine Material Tribology ; Strategic Priority Research Program of the Chinese Academy of Sciences
源URL[http://ir.imr.ac.cn/handle/321006/167055]  
专题金属研究所_中国科学院金属研究所
通讯作者Xue, Weihai; Duan, Deli
作者单位1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式
GB/T 7714		 Wang, Jianfei,Xue, Weihai,Gao, Siyang,et al. Effect of groove surface texture on the fretting wear of Ti-6Al-4V alloy[J]. WEAR,2021,486:11.
APA Wang, Jianfei,Xue, Weihai,Gao, Siyang,Li, Shu,&Duan, Deli.(2021).Effect of groove surface texture on the fretting wear of Ti-6Al-4V alloy.WEAR,486,11.
MLA Wang, Jianfei,et al."Effect of groove surface texture on the fretting wear of Ti-6Al-4V alloy".WEAR 486(2021):11.

入库方式： OAI收割

来源：金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。