Effect of Annealing Temperature and Strain Rate on Mechanical Property of a Selective Laser Melted 316L Stainless Steel
文献类型:期刊论文
作者 | Jiang, Hua-Zhen2,3; Li, Zheng-Yang2,3; Feng, Tao1; Wu, Peng-Yue1; Chen, Qi-Sheng2,3; Yao, Shao-Ke2,3; Hou, Jing-Yu2,3; Yao SK(姚少科); Li ZY(李正阳); Li ZY(李正阳) |
刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS |
出版日期 | 2021-11-05 |
页码 | 17 |
ISSN号 | 1006-7191 |
关键词 | Selective laser melting 316L stainless steel Heat treatment Strain hardening behaviors Mechanical property |
DOI | 10.1007/s40195-021-01342-x |
通讯作者 | Li, Zheng-Yang(zyli@imech.ac.cn) ; Chen, Qi-Sheng(qschen@imech.ac.cn) |
英文摘要 | In the present work, 316L stainless steel specimens are fabricated by selective laser melting (SLM) via optimized laser process parameters. The effects of two extrinsic factors, i.e., strain rate and annealing temperature, on the mechanical performance of SLM-processed parts are studied. The two intrinsic factors, namely strain rate sensitivity m and work hardening exponent n, which control the tensile properties of the as-built samples, are quantified. Microstructure characterizations show that cellular structure and crystalline grain exhibit apparently different thermal stability at 873 K. Tensile testing reveals that the yield strength decreases from 584 +/- 16 MPa to 323 +/- 2 MPa, while the elongation to failure increases from (46 +/- 1)% to (65 +/- 2)% when annealing temperature varies from 298 K to 1328 K. The n value increases from 0.13 to 0.33 with the increase in annealing temperature. Due to the presence of fine cellular structures and high relative density achieved in as-printed 316L samples, a strong dependence between tensile yield strength and strain rate is observed. In addition, the strain rate sensitivity of the SLM-produced 316L part (m = 0.017) is much larger than that of conventional coarse-grained part (m = 0.006), whereas the n value increases slightly from 0.097 to 0.14 with increasing strain rate. |
WOS关键词 | RATE SENSITIVITY ; PROCESS PARAMETERS ; HEAT-TREATMENT ; CORROSION BEHAVIOR ; HIGH-STRENGTH ; MICROSTRUCTURE ; DUCTILITY ; POROSITY ; NETWORK ; PARTS |
资助项目 | National Natural Science Foundation of China[11772344] ; National Key R&D Program of China[2016YFB1100700] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
WOS记录号 | WOS:000714874800002 |
资助机构 | National Natural Science Foundation of China ; National Key R&D Program of China |
源URL | [http://dspace.imech.ac.cn/handle/311007/87963] |
专题 | 力学研究所_国家微重力实验室 宽域飞行工程科学与应用中心 |
通讯作者 | Li, Zheng-Yang; Chen, Qi-Sheng |
作者单位 | 1.Beijing E Plus 3D Technol Co LTD, Beijing 102299, Peoples R China 2.Chinese Acad Sci, Inst Mech, Beijing 100190, Peoples R China 3.Univ Chinese Acad Sci, Sch Engn Sci, Beijing 100190, Peoples R China |
推荐引用方式 GB/T 7714 | Jiang, Hua-Zhen,Li, Zheng-Yang,Feng, Tao,et al. Effect of Annealing Temperature and Strain Rate on Mechanical Property of a Selective Laser Melted 316L Stainless Steel[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2021:17. |
APA | Jiang, Hua-Zhen.,Li, Zheng-Yang.,Feng, Tao.,Wu, Peng-Yue.,Chen, Qi-Sheng.,...&候静宇.(2021).Effect of Annealing Temperature and Strain Rate on Mechanical Property of a Selective Laser Melted 316L Stainless Steel.ACTA METALLURGICA SINICA-ENGLISH LETTERS,17. |
MLA | Jiang, Hua-Zhen,et al."Effect of Annealing Temperature and Strain Rate on Mechanical Property of a Selective Laser Melted 316L Stainless Steel".ACTA METALLURGICA SINICA-ENGLISH LETTERS (2021):17. |
入库方式: OAI收割
来源:力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。